... range 33-38 mole % CdGa2S , two micro- hardnesses are observed 2.84 × 109 and 3.82 × 109 N m - 2 , which are almost constant within this concentration range . The density ( Fig . 2b ) falls from 5.30 × 103 to 4.79 x 103 kg m in the range ...
... range 33-38 mole % CdGa2S , two micro- hardnesses are observed 2.84 × 109 and 3.82 × 109 N m - 2 , which are almost constant within this concentration range . The density ( Fig . 2b ) falls from 5.30 × 103 to 4.79 x 103 kg m in the range ...
Trang 1675
... range of solid solutions Na , Sc2 ( 1 - x ) Fe2x ( PO4 ) 3 in the complete range 0 ≤ x ≤ 1. The X - ray powder diffraction patterns of the solid solutions in the range 0.02 < x < 0.92 are indexed satisfactorily by assuming ...
... range of solid solutions Na , Sc2 ( 1 - x ) Fe2x ( PO4 ) 3 in the complete range 0 ≤ x ≤ 1. The X - ray powder diffraction patterns of the solid solutions in the range 0.02 < x < 0.92 are indexed satisfactorily by assuming ...
Trang 1703
... range 350-450 ° C . After the synthesis , the specimens containing 0–8 mole % Yb2Se , were obtained in the vitreous form . The conchoidal fracture and the absence of diffraction lines from the X - ray diffraction patterns and of ...
... range 350-450 ° C . After the synthesis , the specimens containing 0–8 mole % Yb2Se , were obtained in the vitreous form . The conchoidal fracture and the absence of diffraction lines from the X - ray diffraction patterns and of ...
Nội dung
Inorganic | 1245 |
brackets correspond to the Russian original | 1403 |
Journal | 1559 |
Bản quyền | |
2 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1984 Translated absorption acetonitrile acid anions aqueous solution atoms bands bond calculated cations Chem chemical Chemistry chloride cm¹ cobalt cobalt(II complexes components composition compounds concentration constant containing coordination copper(II corresponding crystallisation crystals curves decrease determined electron endothermic equilibrium diagram eutectic experimental extraction Figure formation formed groups H₂O heating hydrated hydrogen increase infrared spectra Inorg ionic ions iron(III isothermal Khim Khimiya lanthanide lattice ligand liquid magnesium melts metal method mixture mole mole¹ molecules molybdates molybdenum Moscow Nauk SSSR Neorg nitrate obtained oxide oxygen palladium(II parameters platinum(II potassium range ratio reaction rhodium rhodium(III Russ Russ.J salt shows sodium solid phases solid solutions solubility solvent specimens spectra spectrum stability structure studied synthesis Table temperature terbium ternary thermal analysis thermal decomposition thermodynamic tion Translated from Zhurnal values vanadium wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii