... mole - 1 . According to the results of Foote and Fleischer ' , the heat of dissociation of Rb [ I ( I ) 2 ] calculated from the solubility of iodine in benzene ( the RbI - I2 - CH , system ) at 6 ° and 25 ° C is 17.2 kcal mole - 1 . It ...
... mole - 1 . According to the results of Foote and Fleischer ' , the heat of dissociation of Rb [ I ( I ) 2 ] calculated from the solubility of iodine in benzene ( the RbI - I2 - CH , system ) at 6 ° and 25 ° C is 17.2 kcal mole - 1 . It ...
Trang 1267
... mole % ( 52 wt . % ) CaWO1 , and showed a eutectic at 2.5 mole % ( 15 wt . % ) CaWO4 , 588 ° . In the CaWO - KC1 system there is a eutectic at 1.42 mole % ( 5.3 wt . % ) CaWO1 , 762 ° and in the CaWO , -NaCl system one at 1.35 mole ...
... mole % ( 52 wt . % ) CaWO1 , and showed a eutectic at 2.5 mole % ( 15 wt . % ) CaWO4 , 588 ° . In the CaWO - KC1 system there is a eutectic at 1.42 mole % ( 5.3 wt . % ) CaWO1 , 762 ° and in the CaWO , -NaCl system one at 1.35 mole ...
Trang 1268
... mole % CaWO . CaWO - NaCl . Table 2 and Fig . 3 give our results . The liquidus was followed up to 5.4 mole % . The eutectic is at CaWO , 1.5 mole % , 796 ° , not at the temperature given by Anikin3 , 745 ° . Our heating curves confirm ...
... mole % CaWO . CaWO - NaCl . Table 2 and Fig . 3 give our results . The liquidus was followed up to 5.4 mole % . The eutectic is at CaWO , 1.5 mole % , 796 ° , not at the temperature given by Anikin3 , 745 ° . Our heating curves confirm ...
Nội dung
INORGANIC | 825 |
with arsine impurity | 833 |
JOURNAL | 1069 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption spectra Akad alkali amine ammonia ammonium analysis anhydrous anion aqueous solution atoms bond boric acid cadmium caesium calculated cation cerium Chem chemical Chemistry chloride composition compounds concentration constant containing coordination copper hydroxide corresponding crystallisation crystals curve density determined energy enthalpies of formation equation europium eutectic experimental formed g-ion H₂O halides heating hydrate hydrochloric acid hydrogen hydroxide sulphate Inorg ionic ions isotherm kcal Khim lanthanum lattice ligands liquid liquidus lithium litre melting metal method mixture molar mole mole-¹ molecules NaCl Nauk SSSR neodymium Neorg nitrate Obshch obtained optical density oxalate oxide oxygen peritectic potassium precipitate pyridine ratio reaction rubidium Russ salt scandium shows sodium solid phase solid solutions solu solubility specimens stability studied Table temperature terbium thermal decomposition thorium tion values vapour X-ray yttrium Zhur zinc zirconium