... Liquidus temperature , LaCl , SmCl , ° C Composition , mole % LaCl , SmCl , Liquidus temperature , 0 10.68 100 665 61.45 38.55 800 89.32 690 70.12 29.88 812 22.51 77.49 718 88.78 11.22 860 30.58 69.42 736 100 0 852 42.71 57.29 49.25 764 ...
... Liquidus temperature , LaCl , SmCl , ° C Composition , mole % LaCl , SmCl , Liquidus temperature , 0 10.68 100 665 61.45 38.55 800 89.32 690 70.12 29.88 812 22.51 77.49 718 88.78 11.22 860 30.58 69.42 736 100 0 852 42.71 57.29 49.25 764 ...
Trang 1260
... liquidus during heating and cooling coincide at InAs con- centrations between 9 and 100 mole % . On heating alloys with 9 mole % InAs , the liquidus temperature rises from 610 ° for a composition with 9 mole % InAs to 621 ° for pure ...
... liquidus during heating and cooling coincide at InAs con- centrations between 9 and 100 mole % . On heating alloys with 9 mole % InAs , the liquidus temperature rises from 610 ° for a composition with 9 mole % InAs to 621 ° for pure ...
Trang 1271
... liquidus , because when it can be employed it gives the most accurate determinations of the equilibrium temperatures of the liquidus . The technique was as used before 5. To avoid the presence of hydrolysis products , the ampoules were ...
... liquidus , because when it can be employed it gives the most accurate determinations of the equilibrium temperatures of the liquidus . The technique was as used before 5. To avoid the presence of hydrolysis products , the ampoules were ...
Nội dung
INORGANIC | 825 |
with arsine impurity | 833 |
JOURNAL | 1069 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption spectra Akad alkali amine ammonia ammonium analysis anhydrous anion aqueous solution atoms bond boric acid cadmium caesium calculated cation cerium Chem chemical Chemistry chloride composition compounds concentration constant containing coordination copper hydroxide corresponding crystallisation crystals curve density determined energy enthalpies of formation equation europium eutectic experimental formed g-ion H₂O halides heating hydrate hydrochloric acid hydrogen hydroxide sulphate Inorg ionic ions isotherm kcal Khim lanthanum lattice ligands liquid liquidus lithium litre melting metal method mixture molar mole mole-¹ molecules NaCl Nauk SSSR neodymium Neorg nitrate Obshch obtained optical density oxalate oxide oxygen peritectic potassium precipitate pyridine ratio reaction rubidium Russ salt scandium shows sodium solid phase solid solutions solu solubility specimens stability studied Table temperature terbium thermal decomposition thorium tion values vapour X-ray yttrium Zhur zinc zirconium