Russian Journal of Inorganic Chemistry, Tập 24,Trang 959-1906Chemical Society., 1979 |
Từ bên trong sách
Kết quả 1-3 trong 83
Trang 1102
... crystals , medium - sized ditto , growth direc tion [ 100 ] small , columnar crystals dense ceramic yellow , transparent ditto white , matt small crystals a 4.195 A BaHfO 3 2500 perovskite , cubic ditto a = 4.174 A BaZrO3 - BaHfO3 2600 ...
... crystals , medium - sized ditto , growth direc tion [ 100 ] small , columnar crystals dense ceramic yellow , transparent ditto white , matt small crystals a 4.195 A BaHfO 3 2500 perovskite , cubic ditto a = 4.174 A BaZrO3 - BaHfO3 2600 ...
Trang 1482
... crystal plates of thickness up to 0.2 cm and area up to 2.5 cm2 . In some cases the single crystals reached a thickness of 0.6 cm . The angles between the normal of the large plates and the vertical axis of the crucible were close to 60 ...
... crystal plates of thickness up to 0.2 cm and area up to 2.5 cm2 . In some cases the single crystals reached a thickness of 0.6 cm . The angles between the normal of the large plates and the vertical axis of the crucible were close to 60 ...
Trang 1484
... crystals of the y - modification . Similar results were obtained in the preparation of these single crystals from the molten dim olybdate at 550-600 ° C ( specimen K2M 0207 + 8M 003 + 5K2CO3 + M2O3 ) . As noted above , the high ...
... crystals of the y - modification . Similar results were obtained in the preparation of these single crystals from the molten dim olybdate at 550-600 ° C ( specimen K2M 0207 + 8M 003 + 5K2CO3 + M2O3 ) . As noted above , the high ...
Nội dung
COORDINATION solution | 959 |
JOURNAL | 1119 |
JOURNAL | 1279 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption bands acid Akad analysis anion aqueous solution atoms caesium calculated Chem chemical Chemistry chloride cm-¹ cm¹ cobalt(II complex formation components composition compounds concentration coordination copper(II corresponding crystallisation crystals curves decomposition decrease determined dinitrogen tetroxide ditto equilibrium diagram europium eutectic experimental extraction Figure formed g-ion H₂O hafnium heating hydrated hydrogen hydroxide increase infrared spectra Inorg interaction ionic ions isotherms kcal Khim Khimiya lanthanide lattice ligand lithium mass melting mercury(II metal method mixture mole mole¹ molecules Moscow Nauk SSSR Neorg nickel(II niobium nitrate obtained optical density oxide oxygen parameters phosphate potassium precipitate protons range ratio reaction rhenium(VII rubidium Russ salts scandium shows sodium solid phases solid solutions solubility solvent specimens spectrum stability constants structure studied sulphate sulphuric Table temperature ternary thermal tion Translated from Zhurnal vibrations wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhurnal Neorganicheskoi Khimii zirconium