... copper are grown by oriented solidification using the vertical Bridgman technique . The effective segregation coefficient Kef of copper in ZnAs2 is found to be 0.49 at a solid- ification rate of 0.5 mm / h and the initial concentration ...
... copper are grown by oriented solidification using the vertical Bridgman technique . The effective segregation coefficient Kef of copper in ZnAs2 is found to be 0.49 at a solid- ification rate of 0.5 mm / h and the initial concentration ...
Trang 708
... copper is displaced to the end of the single crystal ( Fig . 1 ) . This indicates that the segregation coefficient of copper in ZnAs , is less than unity . The approximate Kef value was found from the following condition : at g = 0 c 0 ...
... copper is displaced to the end of the single crystal ( Fig . 1 ) . This indicates that the segregation coefficient of copper in ZnAs , is less than unity . The approximate Kef value was found from the following condition : at g = 0 c 0 ...
Trang 865
... Copper precipitates at a pH of approximately 5 ; the reac- tion must be terminated at pH 5.8 - 6.0 . If the pH is out of the range specified , it should be adjusted to 5.9 ± 0.1 . The precipitated copper hydroxo salts are washed ...
... Copper precipitates at a pH of approximately 5 ; the reac- tion must be terminated at pH 5.8 - 6.0 . If the pH is out of the range specified , it should be adjusted to 5.9 ± 0.1 . The precipitated copper hydroxo salts are washed ...
Nội dung
MAY 30 | 687 |
Synthesis and Properties of Inorganic Compounds | 699 |
Effective Segregation Coefficient of Copper in ZnAs₂ | 707 |
27 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid addition amount analysis anion approximately aqueous atoms bands bismuth bond calculated cations central atom Chem chemical Chemistry cm-¹ complexes components composition compounds concentration considered constant containing coordination copper Copyright corresponding crystal curves decomposition decrease dependence described determined diffraction distribution effect electron elements energy experimental extraction fact formation heating higher hydrogen increase indicates Inorganic intensities interaction ions kcal/mol Khim ligand measured metal method mixture molecules Moscow nature Neorg Note observed obtained occurs organic oxide oxygen parameters peak performed phase podands position possible potassium powder prepared presents properties Publishing range ratio reaction REFERENCES region respectively Russian salts sample Sciences shows similar sodium solid solution space group spectra spectrum stability structure studied synthesis Table temperature thermal tion transition values vibrations weight X-ray