Russian Journal of Inorganic Chemistry, Tập 32,Trang 619-1220Chemical Society, 1987 |
Từ bên trong sách
Kết quả 1-3 trong 84
Trang 907
... solid solutions based on y - Bi2MOO seems improbable . Even if it is assumed that the formation of a solid solution stabilises the low - temperature modification ( similar to the behaviour described for the Bi2MoO - Bi2WO6 system ) ...
... solid solutions based on y - Bi2MOO seems improbable . Even if it is assumed that the formation of a solid solution stabilises the low - temperature modification ( similar to the behaviour described for the Bi2MoO - Bi2WO6 system ) ...
Trang 1017
... solid solutions based on PbTe increases from 620 MPa for PbTe to 1400 MPa to the solid solution ( PbTe ) 0.97Fe0.03 , then Hu remains constant for com- positions up to 70 mole % PbTe . The microhardness of the dark grey phase , that is ...
... solid solutions based on PbTe increases from 620 MPa for PbTe to 1400 MPa to the solid solution ( PbTe ) 0.97Fe0.03 , then Hu remains constant for com- positions up to 70 mole % PbTe . The microhardness of the dark grey phase , that is ...
Trang 1061
... solid solutions based on calcium orthovanadate are in equilibrium with phases which exist in the Ca ̧ ( VO4 ) 2- NaCAVO - EUVO system . The region of existence of the solid solutions is bounded by the figure abcd . The greatest common ...
... solid solutions based on calcium orthovanadate are in equilibrium with phases which exist in the Ca ̧ ( VO4 ) 2- NaCAVO - EUVO system . The region of existence of the solid solutions is bounded by the figure abcd . The greatest common ...
Nội dung
Journal of QDI 761 | 619 |
The synthesis and study of lanthanide bishydroxy | 626 |
The calculation of various physicochemical properties | 632 |
Bản quyền | |
6 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acetate acid ammonium anions aqueous solution atoms bands bond calcium calculated cations Chem chemical Chemistry chloride chromium(III cm-¹ cm¯¹ cm¹ cobalt(II complex formation components composition concentration containing coordination compounds copper(II corresponding crystallisation crystals curves decrease determined EDTA electronic endothermic equilibrium diagram ethanol europium eutectic experimental extraction Figure formed H₂O heating hydrate hydrogen hydroxide i.r. spectra increase indicates infrared spectra Inorg ions iron(II isotherms Khim lanthanide lattice ligand liquid lithium manganese(II mass loss metal method mixture mole Moscow Nauk SSSR Neorg nickel(II nitrate obtained oxide oxygen parameters plexes potassium precipitate range reaction Russ Russ.J salt sodium solid phase solid solutions solubility specimens spectra spectrum structure studied sulphate synthesis temperature ternary thermal analysis thermal decomposition tion Translated from Zhurnal values vibrations water molecules wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii zirconium