Russian Journal of Inorganic Chemistry, Tập 41,Trang 683-1012Chemical Society., 1996 |
Từ bên trong sách
Kết quả 1-3 trong 9
Trang 891
... lanthanum ( or neodymium ) , and alumi- num oxalates , carbonates , or hydroxides . To prepare SrLaGaO4 , we used only the corresponding oxalates or carbonates . The starting materials were reagent - grade stron- tium , lanthanum ...
... lanthanum ( or neodymium ) , and alumi- num oxalates , carbonates , or hydroxides . To prepare SrLaGaO4 , we used only the corresponding oxalates or carbonates . The starting materials were reagent - grade stron- tium , lanthanum ...
Trang 892
... lanthanum , and aluminum nitrates mixed in the molar ratio 1 1 : 1. The mixed solution was slowly ( 60-70 drops per minute ) added to a 14 % solution of ammonium oxalate . The pH of the latter solution was maintained at 10 by adding ...
... lanthanum , and aluminum nitrates mixed in the molar ratio 1 1 : 1. The mixed solution was slowly ( 60-70 drops per minute ) added to a 14 % solution of ammonium oxalate . The pH of the latter solution was maintained at 10 by adding ...
Trang 943
... lanthanum and europium tris ( acetylacetonate ) s ( table , compounds 7 , 8 ) . • The table shows that the structure ... lanthanum ( III ) complexes are of most interest . Because lanthanum complexes are the most unstable rare - earth ...
... lanthanum and europium tris ( acetylacetonate ) s ( table , compounds 7 , 8 ) . • The table shows that the structure ... lanthanum ( III ) complexes are of most interest . Because lanthanum complexes are the most unstable rare - earth ...
Nội dung
Synthesis and Properties of Inorganic Compounds | 695 |
Thermal Dissociation of Ca₂CuO | 703 |
Thermolysis of Antimony Pentoxide Hydrate at the First Stage of the Reduction of SbV to SbIII | 711 |
Bản quyền | |
17 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acetylacetonate acid amorphous analysis anion annealing apatite atoms benzotriazole bismuth bond lengths CaO2 carbon cations ceramic chelate chelate cycles Chem chemical cm-¹ complexes composition compounds concentration containing coordination copper corresponding crystals cubes cuprate curves decomposition decrease determined diffraction patterns electron English Translation Copyright enthalpy eutectic experimental films fluorine formation fragments glass glass-formation H₂O Hayka/Interperiodica Publishing Russia heating high-temperature HTSC hydrogen increase Inorg intensity ions Khim lanthanide lanthanum ligand liquid MAHK Hayka/Interperiodica Publishing manganese(II melt metal method mixture molecules Moscow Neorg obtained Original Russian Text oxide oxygen peak peritectic perovskite phase diagram properties quinaldic acid Raman range ratio reaction region Russia Received Russian Academy Russian Text Copyright samples solid solutions solubility space group spectra spectrum structure studied sulfate superconducting synthesis Table temperature ternary system thermal tion ture unit cell parameters vibrations X-ray diffraction X-ray powder diffraction yttrium zinc