Russian Journal of Inorganic Chemistry, Tập 41,Trang 683-1012Chemical Society., 1996 |
Từ bên trong sách
Kết quả 1-3 trong 38
Trang 817
... addition of 2 mol % H2SO4 to the Al2 ( SO4 ) 3 · 11H2O glass does not have a significant effect on the Tg , Ter ( crystallization tem- perature ) , and Tm ( melting temperature ) . A further increase in the acid concentration leads to a ...
... addition of 2 mol % H2SO4 to the Al2 ( SO4 ) 3 · 11H2O glass does not have a significant effect on the Tg , Ter ( crystallization tem- perature ) , and Tm ( melting temperature ) . A further increase in the acid concentration leads to a ...
Trang 994
... Addition of MnCl2 ( 5 , 7 , 7.5 mol / l ) into NaPO3 melt causes a shift of the absorption edge of NaPO , to ca. 38000 cm- and emergence of d - d bands ( 16000-30000 cm - 1 ) , characteristic of a manganese ( II ) complex ( Fig . 1 ...
... Addition of MnCl2 ( 5 , 7 , 7.5 mol / l ) into NaPO3 melt causes a shift of the absorption edge of NaPO , to ca. 38000 cm- and emergence of d - d bands ( 16000-30000 cm - 1 ) , characteristic of a manganese ( II ) complex ( Fig . 1 ...
Trang 1009
... addition , the larger atomic weight of mercury rela- tive to cadmium results in the shift of the edge of the transmission band in the IR range farther than 20 μm . Before studying glass formation in the ZnBr2 - HgBr2- CsBr ternary ...
... addition , the larger atomic weight of mercury rela- tive to cadmium results in the shift of the edge of the transmission band in the IR range farther than 20 μm . Before studying glass formation in the ZnBr2 - HgBr2- CsBr ternary ...
Nội dung
Synthesis and Properties of Inorganic Compounds | 695 |
Thermal Dissociation of Ca₂CuO | 703 |
Thermolysis of Antimony Pentoxide Hydrate at the First Stage of the Reduction of SbV to SbIII | 711 |
Bản quyền | |
17 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acetylacetonate acid amorphous analysis anion annealing apatite atoms benzotriazole bismuth bond lengths CaO2 carbon cations ceramic chelate chelate cycles Chem chemical cm-¹ complexes composition compounds concentration containing coordination copper corresponding crystals cubes cuprate curves decomposition decrease determined diffraction patterns electron English Translation Copyright enthalpy eutectic experimental films fluorine formation fragments glass glass-formation H₂O Hayka/Interperiodica Publishing Russia heating high-temperature HTSC hydrogen increase Inorg intensity ions Khim lanthanide lanthanum ligand liquid MAHK Hayka/Interperiodica Publishing manganese(II melt metal method mixture molecules Moscow Neorg obtained Original Russian Text oxide oxygen peak peritectic perovskite phase diagram properties quinaldic acid Raman range ratio reaction region Russia Received Russian Academy Russian Text Copyright samples solid solutions solubility space group spectra spectrum structure studied sulfate superconducting synthesis Table temperature ternary system thermal tion ture unit cell parameters vibrations X-ray diffraction X-ray powder diffraction yttrium zinc