... alloys of a required composition is best achieved by the method of preliminary alloys . Therefore , suitable manganese - copper and manganese - iron binary alloys were first prepared ( Table I ) . The preparation of alloys intended for ...
... alloys of a required composition is best achieved by the method of preliminary alloys . Therefore , suitable manganese - copper and manganese - iron binary alloys were first prepared ( Table I ) . The preparation of alloys intended for ...
Trang 174
... alloys at the initial stages of annealing ( 900-800 ° ) . In a number of alloys with a 50 % and 60 % content of manganese , a dendritic structure was observed after stepwise annealing ( Figure 2b , c ) . Binary manganese - iron alloys ...
... alloys at the initial stages of annealing ( 900-800 ° ) . In a number of alloys with a 50 % and 60 % content of manganese , a dendritic structure was observed after stepwise annealing ( Figure 2b , c ) . Binary manganese - iron alloys ...
Trang 179
... alloys of these compositions do not change their weight . This is explained by the formation , on alloys containing 20 and 30 wt . % of chromium , of a dense chromium oxide film , which at 1200 ° prevents further oxidation . The greater ...
... alloys of these compositions do not change their weight . This is explained by the formation , on alloys containing 20 and 30 wt . % of chromium , of a dense chromium oxide film , which at 1200 ° prevents further oxidation . The greater ...
Nội dung
Berul S I Thermographic Investigation of Potassium Nitrite | 268 |
Author Index | 276 |
I Maltseva N N Fedneva E M | 74 |
Bản quyền | |
2 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
Academy of Sciences alloys ammonia ammonium analysis anhydrous anion anorg aqueous solutions atom beryllium calculated carbonate cesium Chem chemical chloride coefficient complex acids complex compounds composition concentration constant coprecipitation corresponding crystalline crystals decomposition dehydration determined diagram dioxide electrode endothermic equilibrium eutectic experimental ferrite ferrocyanide Figure formed g Pt g substance glaserite H₂O heteropoly acids hydrate hydrochloric acid hydrogen hydrolysis hydroxides Inorganic Chemistry interaction investigation ions isotherm Journal of Inorganic K₂SO4 kcal lanthanum lattice lithium melting metal method mixture molecules moles NaCl NH₂ niobium obtained oxalate oxide oxygen perchloric acid platinum potassium precipitate pyridine ratio reaction Received for publication rhenium ruthenium salt sample solid phase solid solutions SSSR structure substance gave sulfate sulfuric acid synthesis Table temperature ternary thallium thallium iodide thermal thermogram thorium tion titration uranium USSR valency values vapor X-ray photographs ytterbium Zhurnal Neorganicheskoi Khimii