... melting points and the polymorphic transformation temperatures of K , TaF , in an argon atmosphere and in air are given in Table 3. Visual observation of the cooling of the melt shows that the salt crystallises quickly at the melting ...
... melting points and the polymorphic transformation temperatures of K , TaF , in an argon atmosphere and in air are given in Table 3. Visual observation of the cooling of the melt shows that the salt crystallises quickly at the melting ...
Trang 25
... melted in nickel crucible in argon atmosphere melted in platinum crucible in air ل السالبالحليب السيليا سلسل fullly a с X - ray patterns show that , after melting the salt at 830 ° and keeping it at this temperature for 10 min , the ...
... melted in nickel crucible in argon atmosphere melted in platinum crucible in air ل السالبالحليب السيليا سلسل fullly a с X - ray patterns show that , after melting the salt at 830 ° and keeping it at this temperature for 10 min , the ...
Trang 339
... melting point then decreases sharply and rises very slowly from TiCl . n - C ̧H11COOC2H ̧ onwards . 11 The dependence of the melting points of the esters on the number of carbon atoms in the acid radical ( Table 3 ) follows the opposite ...
... melting point then decreases sharply and rises very slowly from TiCl . n - C ̧H11COOC2H ̧ onwards . 11 The dependence of the melting points of the esters on the number of carbon atoms in the acid radical ( Table 3 ) follows the opposite ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption spectra acetate acid Akad alkali alloys ammonia ammonium analysis anhydrous anion aqueous solutions atom beryllium bond caesium calcium calculated carbon cations Chem chemical chloride cm-¹ cm² coefficient complex composition compounds concentration constant corresponding crystallisation crystals decomposition determined dissociation dissolved equilibrium diagram ether ethylenediamine eutectic extraction filtered formation formed H₂O hydrates hydrochloric acid hydrogen hydrolysis hydroxide increase indium infrared Inorg ions iridium isotherm kcal Khim LiCl ligand melting metal methanol method mixture molar mole mole-¹ molecules molybdate molybdenum Moscow NaCl NaOH Nauk SSSR Neorg niobium nitrobenzene Obshch obtained oxide potassium precipitate ratio reaction reciprocal system rhodium Russ salts shows sodium solid phase solid solutions solu solubility solvent specimens studied substance sulphates sulphide sulphuric Table tantalum temperature ternary system thermal thiooxine thorium tion titration values vanadium vapour pressure water molecules X-ray Zhur zinc