A phase analysis of the formates prepared , and the products of thermolysis and annealing of their mixtures was ... at T≥ 700 ° C . This induces melting of the reaction mixture to form a glassy mass , which crystallizes very slowly .
A phase analysis of the formates prepared , and the products of thermolysis and annealing of their mixtures was ... at T≥ 700 ° C . This induces melting of the reaction mixture to form a glassy mass , which crystallizes very slowly .
Trang 1031
The thermal decomposition of the mixture La ( CH3COO ) 3 · 1.5H2O + 0.81Cu ( CH3COO ) 1⁄2 · H2O + 0.19Ni ( HCOO ) 2 · 2H2O is as complex as the process considered above . Figure 2 indicates that the water loss is completed at about 170 ...
The thermal decomposition of the mixture La ( CH3COO ) 3 · 1.5H2O + 0.81Cu ( CH3COO ) 1⁄2 · H2O + 0.19Ni ( HCOO ) 2 · 2H2O is as complex as the process considered above . Figure 2 indicates that the water loss is completed at about 170 ...
Trang 1388
The cathodic deposit at i > 20 × 102 A / m2 is a powdery mixture of W2C and WC with tungsten . The electrolytic product obtained at i < 5 × 102 A / m2 is the mixture of W2C with carbon . The deposition rate of WC in the studied range of ...
The cathodic deposit at i > 20 × 102 A / m2 is a powdery mixture of W2C and WC with tungsten . The electrolytic product obtained at i < 5 × 102 A / m2 is the mixture of W2C with carbon . The deposition rate of WC in the studied range of ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Vol 40 No 7 | 1021 |
Synthesis of LaCu₁ NiO2 5 +8 from Carboxylates | 1030 |
Synthesis and Some Properties of Single Crystals of the ZnGd₁S and ZnSSe₁ Solid Solutions | 1039 |
Bản quyền | |
7 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption Academy of Sciences according acid activity addition analysis angles anion aqueous atoms bands bond calculated cation cell changes Chem chemical Chemistry cm-¹ complexes composition compounds concentration constants containing coordination copper Copyright corresponding crystals curves decomposition decrease dependence described determined distances effect electron energy equilibrium experimental extraction fact fluoride formation groups H₂O heating hydrogen increase indicates initial Inorganic Institute intensity interaction ions Khim ligand lines melt metal method mixture mol/l molecules Moscow Neorg Note observed obtained occurs oxide oxygen parameters phase position powder prepared presented pressure properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples shift shows similar sodium solid solubility solutions space group spectra spectrum stability structure studied synthesis Table temperature tetrahedral thermal tion Translation values vibrations X-ray diffraction
Thông tin thư mục
| Tiêu đề | Russian Journal of Inorganic Chemistry, Tập 40,Trang 1021-1526 |
| Cộng tác viên | British Library. Lending Division, Royal Society of Chemistry (Great Britain), Chemical Society (Great Britain), Akademii︠a︡ nauk SSSR. |
| Nhà xuất bản | British Library Lending Division with the cooperation of the Royal Society of Chemistry, 1995 |
| Nguyên bản từ | Đại học Michigan |
| Đă được số hóa | 9 Tháng 4 2010 |
| Xuất lời trích dẫn | BiBTeX EndNote RefMan |