Russian Journal of Inorganic Chemistry, Tập 29,Trang 1245-1836Chemical Society, 1984 |
Từ bên trong sách
Kết quả 1-3 trong 83
Trang 1341
... phase . The homoge- nisation temperature falls steadily as the WO3 concentration is increased , from 1240 ° at 0 % WO3 to 900 ° C at 25 % WO3 . The orthorhombic phase with the TTB structure type has a limiting composition of 27.5 % WO3 ...
... phase . The homoge- nisation temperature falls steadily as the WO3 concentration is increased , from 1240 ° at 0 % WO3 to 900 ° C at 25 % WO3 . The orthorhombic phase with the TTB structure type has a limiting composition of 27.5 % WO3 ...
Trang 1363
... Phase relations in Ca1 ( VO4 ) 2 - MVO ( M = La , Sm , Eu ) systems have been studied . Solid solutions Ca3 ( 1 - x ) M2x ( VO4 ) 2 with 0 < x < 0.12 having the calcium orthovanadate structure are formed . In the Ca3 ( VO4 ) 2 - LaVO4 ...
... Phase relations in Ca1 ( VO4 ) 2 - MVO ( M = La , Sm , Eu ) systems have been studied . Solid solutions Ca3 ( 1 - x ) M2x ( VO4 ) 2 with 0 < x < 0.12 having the calcium orthovanadate structure are formed . In the Ca3 ( VO4 ) 2 - LaVO4 ...
Trang 1433
... phase z ** 1 : 0.97 1.10 1.16 a - phase + phase z 1 : 1.00 : 1.01 : 3.99 B - phase 1 : 1.04 1.01 : 3.928 - phase + trace of a - phase Molar ratio in the original mixture Ho3 + PH molar ratio in it . final C204 Ho3 * : F : C202 : H20 Phase ...
... phase z ** 1 : 0.97 1.10 1.16 a - phase + phase z 1 : 1.00 : 1.01 : 3.99 B - phase 1 : 1.04 1.01 : 3.928 - phase + trace of a - phase Molar ratio in the original mixture Ho3 + PH molar ratio in it . final C204 Ho3 * : F : C202 : H20 Phase ...
Nội dung
Russian | 1243 |
Journal | 1401 |
hydrated antimony pentoxide M Li Na | 1412 |
Bản quyền | |
5 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1983 Translated absorption acid alkali metal alloys anion aqueous solution atoms bands bond caesium calculated cation Chem chemical Chemistry chloride cm¹ components composition compounds concentration constant containing coordination copper(II corresponding crown ethers crystallisation crystals curves determined ditto endothermic equilibrium diagram ethanol europium eutectic experimental Figure fluoride formed given in Table H₂O heating hydrated hydrogen hydroxide increase infrared spectra Inorg ionic strength ions isothermal Khim Khimiya lanthanide ligand mass melts method mixture mole mole¹ molybdenum Moscow Nauk SSSR Neorg niobium nitrate obtained oxide oxygen parameters phosphate potassium precipitate present pyrochlore range reaction reagent Russ Russ.J salts scandium shows sodium solid phases solid solutions solid solutions based solubility specimens spectrum structure studied synthesis temperature thermal analysis thermal decomposition tion Translated from Zhurnal uranyl fluoride values vibrations water molecules wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii