Russian Journal of Inorganic Chemistry, Tập 49,Số phát hành 1-4British Library Lending Division with the cooperation of the Royal Society of Chemistry, 2004 |
Từ bên trong sách
Kết quả 1-3 trong 61
Trang 8
... region 1340-1630 cm - 1 . This band is split because of the low symmetry of the carbonate group , which is not an equilateral triangle ( Table 4 ) . Characteristic absorption bands in the region 1040-1070 cm are assigned to the ...
... region 1340-1630 cm - 1 . This band is split because of the low symmetry of the carbonate group , which is not an equilateral triangle ( Table 4 ) . Characteristic absorption bands in the region 1040-1070 cm are assigned to the ...
Trang 220
... region of structural influence of II - B2O3 . Their structures are unknown ; however , at the boundary of this region , neighboring orthoborates LnBO3 crystallize . Thus , surveying predominant orientations of dimers in the above ...
... region of structural influence of II - B2O3 . Their structures are unknown ; however , at the boundary of this region , neighboring orthoborates LnBO3 crystallize . Thus , surveying predominant orientations of dimers in the above ...
Trang 479
... region were recorded on a Specord 61 NIR spectropho- tometer . Samples for the IR spectroscopic study were prepared as polished plates 2 mm thick . The glass formation region in the AgCl - TeO2 - WO3 system , occupying about 25 % of the ...
... region were recorded on a Specord 61 NIR spectropho- tometer . Samples for the IR spectroscopic study were prepared as polished plates 2 mm thick . The glass formation region in the AgCl - TeO2 - WO3 system , occupying about 25 % of the ...
Nội dung
Vol 49 No 1 | 1 |
Isomorphism in the NH44K441UO2CO33 System | 7 |
Conversions of Intermetallic Compounds SmCo and Sm₂Co17 | 13 |
Bản quyền | |
5 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
ų absorption Academy of Sciences acid Acta analysis anions atoms band bond lengths calcd calculated carbon cations chain chelate Chem chemical chloride cm-¹ complexes composition concentration corresponding crystal structure Crystallogr curves decomposition decrease diffraction patterns dimers distances electron energy English Translation Copyright enthalpy experimental formation g/cm³ H₂O heating hydrogen bonds hydroxide Inorg Inorganic Chemistry interaction ionic ions Khim lanthanide ligand magnesium MAIK Nauka/Interperiodica manganese(II metal mixture mol/l molecular Moscow nanotubes Neorg nickel(II nitrate Original Russian Text oxide oxygen atoms Pb atom pentatope phase phosphates Phys plane plexes polyhedra proton range reaction refined Russ Russia Received Russian Academy Russian Journal Russian Text Copyright salt samples sodium solid solutions space group spectra spectrum studied sulfur symmetry synthesis Table temperature thermal parameters thermodynamic thermolysis tion ture unit cell unit cell parameters values water molecules X-ray diffraction X-ray powder diffraction