... various ability to combine with the solvent , i.e. to placement of the NH | ion show that the product is homogene- displace to the right the equilibrium ous , has the composition NH ( Mn ( salo- ) , ( 1,0 ) , ) , and may be Tl ( H ) + n ...
... various ability to combine with the solvent , i.e. to placement of the NH | ion show that the product is homogene- displace to the right the equilibrium ous , has the composition NH ( Mn ( salo- ) , ( 1,0 ) , ) , and may be Tl ( H ) + n ...
Trang 277
... various temperatures . TABLE 4. -Log instability constant of the complex ion ( Ag ( ts ) ; ] * at various temperatures . 1-25 ° 120 ° 1-30 ° 26.77 + 0.08 26.25 + 0.07 25.75 + 0.08 24.80 + 0.08 23.93 + 0.07 12.98 + 0.07 12.76 + 0.08 ...
... various temperatures . TABLE 4. -Log instability constant of the complex ion ( Ag ( ts ) ; ] * at various temperatures . 1-25 ° 120 ° 1-30 ° 26.77 + 0.08 26.25 + 0.07 25.75 + 0.08 24.80 + 0.08 23.93 + 0.07 12.98 + 0.07 12.76 + 0.08 ...
Trang 297
... various temperatures Fig . 2 . Diagram showing the structure and hardness of an alloy of titanium with 19.27 wt . % of vanadium , quenched from 900 ° and kept at various temperatures . Fig . 4. X - ray photographs of titanium alloys ...
... various temperatures Fig . 2 . Diagram showing the structure and hardness of an alloy of titanium with 19.27 wt . % of vanadium , quenched from 900 ° and kept at various temperatures . Fig . 4. X - ray photographs of titanium alloys ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
according acid activity added alcohol alloys alum amount analysis appears aqueous phase atoms basic calculated carbonate Chem chemical chloride coefficient complex components composition compounds concentration conductivity constant containing corresponding crystallisation crystals curve decomposition decrease Dependence described determined diagram distribution ditto effect electrical elements energy equilibrium eutectic excess experimental experiments extraction formation formed given gives heating hydroxide increase indicates initial ions isotherm Khim layer liquid material maximum measured melting metal method mixture mole molecules NaCl Neorg nitrate observed obtained occurs organic oxides phase platinum precipitate prepared presence pressure ratio reaction Received salt separation shown shows sodium solid solid solutions solubility solution stability structure studied Table temperature ternary thermal thermogram tion values vapour various volume Zhur zinc