Russian Journal of Inorganic Chemistry, Tập 5,Số phát hành 1-6British Library Lending Division with the cooperation of the Royal Society of Chemistry, 1960 |
Từ bên trong sách
Kết quả 1-3 trong 78
Trang 68
... phase . 405 phases and the fact that HCl is extracted with several molecules of water . It has been suggested in a number of cases that strong electrolytes are not dissociated in the organic phase ' . That this is not so in the present ...
... phase . 405 phases and the fact that HCl is extracted with several molecules of water . It has been suggested in a number of cases that strong electrolytes are not dissociated in the organic phase ' . That this is not so in the present ...
Trang 72
... phase , 2 in sin organic organic in aqueous phase , phase , phase , Y co Xнсі YHCI aco Xco Separation coef ficient Baci / Co = ансі aco HC1 XHCI X Co aqueou qorganic phase , phase , HCI HCI 0.6 0.06 36 32 28 24 20 16 12 8 Хco 240.04 Q20 ...
... phase , 2 in sin organic organic in aqueous phase , phase , phase , Y co Xнсі YHCI aco Xco Separation coef ficient Baci / Co = ансі aco HC1 XHCI X Co aqueou qorganic phase , phase , HCI HCI 0.6 0.06 36 32 28 24 20 16 12 8 Хco 240.04 Q20 ...
Trang 300
... phase is formed . Thus the addition of vanadium up to 20 % is without significant influence on the stability of the B - phase in titanium - molybdenum - vanadium alloys . The greatest B - phase stability in the range 100 ° -400 ° is ...
... phase is formed . Thus the addition of vanadium up to 20 % is without significant influence on the stability of the B - phase in titanium - molybdenum - vanadium alloys . The greatest B - phase stability in the range 100 ° -400 ° is ...
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
according acid activity added alcohol alloys alum amount analysis appears aqueous phase atoms basic calculated carbonate Chem chemical chloride coefficient complex components composition compounds concentration conductivity constant containing corresponding crystallisation crystals curve decomposition decrease Dependence described determined diagram distribution ditto effect electrical elements energy equilibrium eutectic excess experimental experiments extraction formation formed given gives heating hydroxide increase indicates initial ions isotherm Khim layer liquid material maximum measured melting metal method mixture mole molecules NaCl Neorg nitrate observed obtained occurs organic oxides phase platinum precipitate prepared presence pressure ratio reaction Received salt separation shown shows sodium solid solid solutions solubility solution stability structure studied Table temperature ternary thermal thermogram tion values vapour various volume Zhur zinc