... parameters of the solid solutions were calculated from the unit - cell parameters ( Table and Fig . 2 ) . The curve giving the change in lattice parameter shows a negative departure from Vegard's law . d , g cm - 3 1.8 The interaction ...
... parameters of the solid solutions were calculated from the unit - cell parameters ( Table and Fig . 2 ) . The curve giving the change in lattice parameter shows a negative departure from Vegard's law . d , g cm - 3 1.8 The interaction ...
Trang 1222
... parameters a and c ( Table ) . When these parameters are plotted against the atomic number of the lanthanide a smooth monotonic curve is obtained ( Figure ) , whereas published results give a great scatter in the points . This promoted ...
... parameters a and c ( Table ) . When these parameters are plotted against the atomic number of the lanthanide a smooth monotonic curve is obtained ( Figure ) , whereas published results give a great scatter in the points . This promoted ...
Trang 1337
... parameters of the compounds of the same composi- tions isolated from aqueous solutions " . The difference in the lattice parameters of our RbSb2F , and of that obtained by Tichit and co - workers " is rather significant . There are two ...
... parameters of the compounds of the same composi- tions isolated from aqueous solutions " . The difference in the lattice parameters of our RbSb2F , and of that obtained by Tichit and co - workers " is rather significant . There are two ...
Nội dung
CONTENTS | 923 |
Vibrational spectra of the spinels Zn2SnO4 and Mg₂SnO4 | 932 |
Preparation of sodium and calcium trivanadates | 940 |
Bản quyền | |
1 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1982 Translated absorption Akad anions aqueous solutions atoms bands bismuth bond boric acid calcium calculated cations Chem chemical Chemistry chloride chromium(III cm-¹ cm¯¹ cm¹ components composition compounds concentration constants containing coordination copper(II corresponding crystallisation crystals curves decrease determined ditto electrons endothermic equilibrium diagram ethanol eutectic experimental Figure formed H₂O heating hydrated hydrogen hydrolysis hydroxide increase infrared spectra Inorg interaction investigation ionic ions isotherm Khim lanthanide lattice parameters ligand mass melting metal method mixture mole molecules Moscow Nauk SSSR Neorg nitrate obtained oxide oxygen peritectic platinum(II potassium present protons Raman range ratio reaction region Russ Russ.J salt shows sodium solid phases solid solutions solid-phase synthesis solubility specimens spectrum structure studied sulphate synthesis temperature thallium thermal decomposition tion Translated from Zhurnal vanadates vanadium vibrations wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii