It was found , that during the chlorination of the mixture of oxides , the rate of the sublimation of SnCl ... of chlorine with binary grade tin dioxide with the specific surface of 10 and oxide mixtures showed that the mutual effect of ...
It was found , that during the chlorination of the mixture of oxides , the rate of the sublimation of SnCl ... of chlorine with binary grade tin dioxide with the specific surface of 10 and oxide mixtures showed that the mutual effect of ...
Trang 1698
Polytherms for the reaction of chlorine with SnO2 ( 1 ) , Fe2O3 ( 2 ) , the mixture contained 99 wt % SnO2 and 1 wt % Fe2O3 ( 3 ) , the mixture contained 50 wt % SnO2 and 50 wt % Fe 03 ( 4 ) . than that of tin tetrachloride .
Polytherms for the reaction of chlorine with SnO2 ( 1 ) , Fe2O3 ( 2 ) , the mixture contained 99 wt % SnO2 and 1 wt % Fe2O3 ( 3 ) , the mixture contained 50 wt % SnO2 and 50 wt % Fe 03 ( 4 ) . than that of tin tetrachloride .
Trang 1699
Transfer of SnClų into the sublimate from the SnO2 + Fe2O3 mixture at 700 ( 1 ) , 750 ( 2 ) , 800 ( 3 ) , and 850 ( 4 ) . - Am is a change in the mass and mo is the initial mass of toward the right . Therefore , the decrease in the rate ...
Transfer of SnClų into the sublimate from the SnO2 + Fe2O3 mixture at 700 ( 1 ) , 750 ( 2 ) , 800 ( 3 ) , and 850 ( 4 ) . - Am is a change in the mass and mo is the initial mass of toward the right . Therefore , the decrease in the rate ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Synthesis and Properties of Inorganic Compounds | 1517 |
Thermal Transformations of AmmoniumLithium Tripolyphosphates T N Galkova and E A Prodant | 1525 |
Synthesis Composition | 1531 |
23 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid ammonium analysis anions appearance aqueous atoms bands bond calculated cations Chem chemical Chemistry chloride coefficients complexes components composition compounds concentration constants containing coordination Copyright corresponding crystals curve decrease dependence described determined diagram diffraction effect electron elements energy equation equilibrium exhibit experimental extraction figure formation formula groups heating increase indicates initial Inorganic intensity interaction ions Khim leads ligand mass measured melting metal method mixed mixture mol/l molecules Moscow Neorg Note observed obtained organic Original oxide oxygen parameters peritectic phase points position possible powder precipitate prepared present pressure properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples shows similar sodium solid solutions spectra spectrum stability structure studied Synthesis Table temperature thermal tion trans Translation values vibrations X-ray