Trang 150
... anneal is presented in Fig . 2 as a function of the batch composition . The T values for the samples of series II , which were annealed in one vessel , and the single point for the sample ( Pr " , Priv ) 2CuO4 with x = 0 , which was ...
... anneal is presented in Fig . 2 as a function of the batch composition . The T values for the samples of series II , which were annealed in one vessel , and the single point for the sample ( Pr " , Priv ) 2CuO4 with x = 0 , which was ...
Trang 151
... annealed samples do not coincide with the batch ratios , but only correlate with them . Thus , it is evident that part of Pr ( IV ) in the start- ing Pro transforms to Pr ( III ) after the first anneal in Series II samples . It is ...
... annealed samples do not coincide with the batch ratios , but only correlate with them . Thus , it is evident that part of Pr ( IV ) in the start- ing Pro transforms to Pr ( III ) after the first anneal in Series II samples . It is ...
Trang 497
... annealed at 600 ° C for 5 days . Visual inspection and X - ray diffraction of the samples annealed at various temperatures showed that the new phase did not form at temperatures below 400 ° C , and it decomposed above 650 ° C ...
... annealed at 600 ° C for 5 days . Visual inspection and X - ray diffraction of the samples annealed at various temperatures showed that the new phase did not form at temperatures below 400 ° C , and it decomposed above 650 ° C ...
Nội dung
Vol 45 No 1 | 2 |
Estimates of the Thermochemical Properties of Mixed Oxides in the CuNbO System | 11 |
Interaction of Natural Borates with Potassium Hydroxide Solution | 17 |
Bản quyền | |
15 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid alkoxides analysis angles anion annealed aqueous atoms band binary bond lengths calcium calculated carbon cation Chem chemical chloride cm-¹ complexes composition compounds concentration coordination corresponding crystal structure curve decrease doping electron English Translation Copyright equation equilibrium experimental extraction fluorine formation gallium gold(III H NMR H₂O hydride hydrogen peroxide increase Inorganic Chemistry interaction ionic ions isomer Khim ligand MAIK Nauka/Interperiodica melting method mixture mol/l molecules molybdates Moscow Nauk Nauka Neorg Novoselova obtained Original Russian Text oxide oxygen atoms phase diagram plexes polyhedron protons range ratio reaction region Russia Received Russian Academy Russian Journal Russian Text Copyright salts samples sodium solid solutions solubility solvates solvent space group spectra spectrum studied synthesis Table temperature ternary thermal thermodynamic tion unit cell unit cell parameters values vanadium vanadium(V vapor VD polyhedra X-ray diffraction X-ray powder diffraction