Russian Journal of Inorganic Chemistry, Tập 2Chemical Society., 1957 |
Từ bên trong sách
Kết quả 1-3 trong 13
Trang 169
... rhodium and platinum alloys containing 6 ; 30 and 40 % of rhodium . After each heating for 1 ; 4 ; 8 , and 12 hours at a temperature of 1700-1800 ° C and 5 ; 15 ; 45 ; and 135 hours at 1550 ° C , measurements of the temf at 1000 ° C ...
... rhodium and platinum alloys containing 6 ; 30 and 40 % of rhodium . After each heating for 1 ; 4 ; 8 , and 12 hours at a temperature of 1700-1800 ° C and 5 ; 15 ; 45 ; and 135 hours at 1550 ° C , measurements of the temf at 1000 ° C ...
Trang 176
... rhodium content of the alloy . The data for platinum and rhodium while not confirming this conclusion , does not eliminate it , but only indicates a high sensitivity of the temf to small quantities of contaminants , the entry of which ...
... rhodium content of the alloy . The data for platinum and rhodium while not confirming this conclusion , does not eliminate it , but only indicates a high sensitivity of the temf to small quantities of contaminants , the entry of which ...
Trang 178
... rhodium and platinum alloys containing more than 10 % rhodium show the phenomenon of " damping " ( extinction ) caused by a considerable increase in the total radiation coeffi- cient . 3. Changes of the temf and loss of weight in rhodium ...
... rhodium and platinum alloys containing more than 10 % rhodium show the phenomenon of " damping " ( extinction ) caused by a considerable increase in the total radiation coeffi- cient . 3. Changes of the temf and loss of weight in rhodium ...
Nội dung
N Georgii Grigorevich Urazov | 1 |
M Shatenshtein A I | 30 |
M Rabinovich B N | 41 |
Bản quyền | |
7 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1957 Zhurnal Neorganicheskoi Academy of Sciences acid alkali alloys aluminum ammonium sulfate annealed basic salt boron trichloride cadmium calculated carbon carnallite cerium Chem coll complex composition concentration copper corresponding crystallization curve determined diagram diborane dioxide dissociation dissolved equilibrium Figure formation formed H₂O heating HNO3 hydride hydrogen hydrolysis hydroxide Inorganic Chemistry investigated ions isotherm isotopes Issledovanie Journal of Inorganic khim lanthanum lattice magnesium magnesium sulfate melting metal method mixture molecules N. S. Kurnakov NaCl nickel nitrate nitrosonitrates obtained oxide oxygen PbCl PbCl₂ Phys Physicochemical Analysis platinum potassium precipitate pyridine pyrosulfates ratio reaction Received for publication refraction rhodium ruthenium samples saturated Section sodium chloride solid phase solid solutions solubility SSSR sulfur sulfuric acid Table temf temperature ternary system thallium thallous iodide thermal thiocyanate tion TiOSO titanium trihydroxyglutaric urea USSR values vanadium weight xanthogenate Zhurnal Neorganicheskoi Khimii