Russian Journal of Inorganic Chemistry, Tập 46,Số phát hành 1-4British Library Lending Division with the cooperation of the Royal Society of Chemistry, 2001 |
Từ bên trong sách
Kết quả 1-3 trong 84
Trang 156
... sample ( sample no . 5 in table ) . reflections from poorly crystallized barium fluoride and from lanthanide oxofluorides . The magnetic susceptibility curve shows the absence of superconductivity down to 12 K for all flu- orinated samples ...
... sample ( sample no . 5 in table ) . reflections from poorly crystallized barium fluoride and from lanthanide oxofluorides . The magnetic susceptibility curve shows the absence of superconductivity down to 12 K for all flu- orinated samples ...
Trang 165
... Sample a , Å AV , % 1a : YNi2 7.184 1b : YNi2 7.154 1c : Yo.95Ni2 14.356 ( 1 ) 1d : YNi2 14.35 ( 1 ) 1e : YNi2 14.27 ( 1 ) 2a : YNi2H3.6 7.583 17.7 2.30 2b : YNi2H3.0 7.569 18.4 2.60 2c : Yo.4Ni2H2.6 15.030 ( 1 ) 14.76 2.62 2d : YNi2H2 ...
... Sample a , Å AV , % 1a : YNi2 7.184 1b : YNi2 7.154 1c : Yo.95Ni2 14.356 ( 1 ) 1d : YNi2 14.35 ( 1 ) 1e : YNi2 14.27 ( 1 ) 2a : YNi2H3.6 7.583 17.7 2.30 2b : YNi2H3.0 7.569 18.4 2.60 2c : Yo.4Ni2H2.6 15.030 ( 1 ) 14.76 2.62 2d : YNi2H2 ...
Trang 167
... sample 4a ) is smaller than that of YNi2H2.88 or YNi2H2.23 and even smaller than that of YNi2 IMC . The aforementioned diffuse peak was once believed to be evidence of the onset of hydride amorphization ( see the above literature survey ) ...
... sample 4a ) is smaller than that of YNi2H2.88 or YNi2H2.23 and even smaller than that of YNi2 IMC . The aforementioned diffuse peak was once believed to be evidence of the onset of hydride amorphization ( see the above literature survey ) ...
Nội dung
Reactions of Tetrabutylammonium Octahydrotriborate with Diborane | 5 |
Interaction of Nickel Oxide with Chlorine | 16 |
A New Ammonium Oxofluorotitanate | 28 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
Academy of Sciences acid ammonium analysis angles anion aqueous solution atoms bond lengths calcd calculated carbon cations chelate Chem chemical shifts chloride cluster cm-¹ complexes composition compounds concentration constant coordination copper(II corresponding crystal structure curve decreases determined diffraction patterns dissociation distances electron energy English Translation Copyright equilibrium experimental extraction fluorine formation fullerene H₂O heating HVCs hydrogen bonds Inorganic Chemistry interaction ions IR spectroscopy Khim kJ/mol ligand lithium MAIK Nauka/Interperiodica metal mixture mol/l Moscow Neorg nitrogen NMR spectra Original Russian Text oxides oxygen palladium(II phase phosphates platinum platinum(IV plexes polymer protons range ratio reaction ring Russia Received Russian Academy Russian Journal Russian Text Copyright sample sodium solid solutions solubility spectroscopy spectrum stability studied synthesis Table temperature thermal tion unit cell parameters values vanadium(V vdWRs vibrations water molecules X-ray diffraction X-ray powder diffraction