... specimens were prepared by prolonged grinding of the oxides in the required proportions ( 5-95 mole % SiO2 ) in an agate mortar , forming into rods with dextrin solu- tion , drying and pre - heating in a Silit furnace at 1000 ° , or ...
... specimens were prepared by prolonged grinding of the oxides in the required proportions ( 5-95 mole % SiO2 ) in an agate mortar , forming into rods with dextrin solu- tion , drying and pre - heating in a Silit furnace at 1000 ° , or ...
Trang 1011
... specimens was found from the porosity and its completeness ascertained also from the change in the slope of the dielectric loss measured before and after 3 h in boiling distilled water . After annealing a disk specimen , silver ...
... specimens was found from the porosity and its completeness ascertained also from the change in the slope of the dielectric loss measured before and after 3 h in boiling distilled water . After annealing a disk specimen , silver ...
Trang 1409
... specimens , by X - ray diffraction studies , by optical ob- servations , and by studying the kinetics of hydrolysis by the method indicated above . The curves for the titration of the specimens ( Fig . 1 ) indicate that at room ...
... specimens , by X - ray diffraction studies , by optical ob- servations , and by studying the kinetics of hydrolysis by the method indicated above . The curves for the titration of the specimens ( Fig . 1 ) indicate that at room ...
Nội dung
JOURNAL of CONTENTS | 771 |
Miscellany | 803 |
SAVITSKII M A TYLKINA I A TSYGANOVA E I GLADYSHEVSKII | 831 |
Bản quyền | |
6 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad alcohol alkali metal alloys ammonium analysis anion atoms caesium calculated cation cerium Chem chemical chloride complex formation components composition compounds concentration conductivity containing corresponding crystallisation crystals curves decomposition determined diagonals dissociation distribution constant double salt endothermic equilibrium diagram eutectic EXPERIMENTAL extraction formed H₂O hafnium heating hydride hydrogen hydrolysis hydroxide increase indicates Inorg ionic ions isomolar series isotherms kcal Khim lanthanum liquid melting methanol method mixture molar ratio mole molecules NaCl Nauk SSSR neodymium Neorg niobium nitrate Obshch obtained optical density oxalate oxalic acid oxide phosphate potassium precipitate prepared reaction reciprocal system resin rhenium Russ saturated scandium shows sodium solid phase solid solutions soln solu solubility specimens spectra stable studied sulphate Table temperature ternary system thallium thermal Thermogram thorium tion uranium uranyl values X-ray Zhur zirconium ZrO2