... eutectic and limited solid solution ( up to 20 % PbSO , ) are formed . The eutectic is at 735 ° and 47 % PbSO ,. V. G. Berg- man2 showed that there is a separate field for a compound x Na2SO..y PbSo , formed at ~ 680 ° , below the ...
... eutectic and limited solid solution ( up to 20 % PbSO , ) are formed . The eutectic is at 735 ° and 47 % PbSO ,. V. G. Berg- man2 showed that there is a separate field for a compound x Na2SO..y PbSo , formed at ~ 680 ° , below the ...
Trang 1094
... eutectic composition . A eutectic was found ( Table 3 and Fig . 3 ) at 45 mole % NaI , 435 ° . The CSF - NaF system was studied by the technique used for the CSC1 - NaCl system , but cooling curves were plotted in this case . The ...
... eutectic composition . A eutectic was found ( Table 3 and Fig . 3 ) at 45 mole % NaI , 435 ° . The CSF - NaF system was studied by the technique used for the CSC1 - NaCl system , but cooling curves were plotted in this case . The ...
Trang 1274
... eutectic is formed 2,3 at 26 % C , 3050 ° . The C - Co system . At the eutectic temperature , 1309 ° , cobalt dissolves about 1 % C , decreasing to 0.1 % as the temperature falls . The ( Co + C ) eutectic 1 contains 2.4 wt . % C. Co ...
... eutectic is formed 2,3 at 26 % C , 3050 ° . The C - Co system . At the eutectic temperature , 1309 ° , cobalt dissolves about 1 % C , decreasing to 0.1 % as the temperature falls . The ( Co + C ) eutectic 1 contains 2.4 wt . % C. Co ...
Nội dung
Journal | 767 |
Journal | 1015 |
Sulphides and oxide sulphides of molybdenum and tungsten | 1021 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad alcohol alkali alloys ammonia ammonium analysis anion aqueous solution atom Blagorod bromide cadmium caesium calculated carbonate cerium Chem chemical chloride CO₂ cobalt coefficient complex composition compounds concentration coordination corresponding crystallisation crystals decomposition determined dissociation equilibrium diagram ether eutectic formation formed H₂O heating curves hydrogen hydroxide increase Inorg Inst ionic ions iridium isotherm kcal Khim lanthanum ligands liquid lithium melting metal method mixture molar ratio mole molecules NaOH Nauk SSSR neodymium Neorg nitrate NO₂ Obshch obtained optical density oxide platinum Platiny Drug potassium precipitate prepared pyridine reaction refractive rubidium Russ salt saturated shows sodium solid phase solid solutions solubility solvents specimens spectra stability studied substance sulphate sulphide sulphuric Table temperature ternary thallium thermal thiourea tin selenide tion titanium trans effect uranium uranyl values X-ray Zhur zirconium