Trang 834
... alloys decreases as the Ag concentra- tion rises ( Fig . 4a ) . The hardness of the alloys quenched from 1200 ° passes through a clearly defined maximum ; this is presumably due to age - hardening since the alloy lies near the boundary ...
... alloys decreases as the Ag concentra- tion rises ( Fig . 4a ) . The hardness of the alloys quenched from 1200 ° passes through a clearly defined maximum ; this is presumably due to age - hardening since the alloy lies near the boundary ...
Trang 835
... alloys . The transforma- tion from the homogeneous into the heterogeneous region is not shown . The maximum on the hardness curve is attri- butable to the alloy Ag 5 , Pd 80 , Rh 15 wt . % , which lies near the boundary of the ẞ - solid ...
... alloys . The transforma- tion from the homogeneous into the heterogeneous region is not shown . The maximum on the hardness curve is attri- butable to the alloy Ag 5 , Pd 80 , Rh 15 wt . % , which lies near the boundary of the ẞ - solid ...
Trang 1076
... alloys , prepared from a hardener alloy , did not lose more than 0.1-0.2 % Ce , whereas the higher cerium alloys , prepared from the pure components , lost 2-3 % Ce . ene . The specimens were annealed in a vacuum at 500 ° and 400 ° ( + ...
... alloys , prepared from a hardener alloy , did not lose more than 0.1-0.2 % Ce , whereas the higher cerium alloys , prepared from the pure components , lost 2-3 % Ce . ene . The specimens were annealed in a vacuum at 500 ° and 400 ° ( + ...
Nội dung
Journal | 767 |
Journal | 1015 |
Sulphides and oxide sulphides of molybdenum and tungsten | 1021 |
Bản quyền | |
24 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad alcohol alkali alloys aluminium ammonia ammonium analysis anion aqueous solution atom Blagorod bromide cadmium caesium calculated carbonate cerium Chem chemical chloride CO₂ cobalt coefficient complex composition compounds concentration coordination cristobalite crystallisation crystals decomposition determined dissociation electrode ether eutectic formation formed H₂O H₂SO hafnium hydrogen hydroxide increase Inorg Inst instability constant ions isotherms kaolinite kcal Khim lanthanum ligand liquid lithium melting metal method mixture molar ratio mole molecules mullite NaOH Nauk SSSR neodymium Neorg nitrate nitrilotriacetic acid NO₂ Obshch obtained optical density oxide platinum Platiny Drug potassium praseodymium precipitate prepared pyridine reaction refractive Russ salt saturated shows sodium solid phase solid solutions solubility solvent stability studied sulphate sulphide sulphuric Table temperature ternary thallium thermal thiourea tin selenide tion titanium trans effect uranium uranyl values X-ray Zhur zirconium