... specimens at each stage of the synthesis . The X - ray diffraction characteristics of the product are given in Table 2. The lattice parameters , a = 9.417 ( 5 ) Å and c = 6.877 ( 4 ) Å , differ from those for the theoretical HA ...
... specimens at each stage of the synthesis . The X - ray diffraction characteristics of the product are given in Table 2. The lattice parameters , a = 9.417 ( 5 ) Å and c = 6.877 ( 4 ) Å , differ from those for the theoretical HA ...
Trang 1451
... specimens for our studies were prepared from " TSRO - 1 " grade ZrO2 , " pure " grade CaO , and " GDO - 1 " grade Gd2O3 by fusing mixtures with the prescribed composition in “ URAN " type apparatus and by solid - state sintering . The ...
... specimens for our studies were prepared from " TSRO - 1 " grade ZrO2 , " pure " grade CaO , and " GDO - 1 " grade Gd2O3 by fusing mixtures with the prescribed composition in “ URAN " type apparatus and by solid - state sintering . The ...
Trang 1457
... specimens from the fluorite - like solid solution region of the ZrO2 - CaO - Gd2O3 system . Mass loss of case specimens ( heated at solid - stage 1200 ° C for 5 h ) , mass % 0.019 * F , F ' ) solid solutions based on the cubic form of ...
... specimens from the fluorite - like solid solution region of the ZrO2 - CaO - Gd2O3 system . Mass loss of case specimens ( heated at solid - stage 1200 ° C for 5 h ) , mass % 0.019 * F , F ' ) solid solutions based on the cubic form of ...
Nội dung
Inorganic | 1353 |
Contents | 1376 |
Activation of the solution of copperII oxide in aqueous EDTA solutions by the 1385 2683 | 1385 |
Bản quyền | |
9 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
acid aluminium ammonia analysis angle anions atoms bands bond calculated Chem chemical Chemistry chloride complex formation complexes composition compounds concentration constants containing coordination copper copper(II corresponding crystal crystal structure crystallisation curves decrease dependence described determined diagram dioxide EDTA electronic energy English translation equilibrium experimental Figure formation formed given gives halides heating hydrogen increase indicates influence infrared Inorg INORGANIC ions Khim kinetic ligand manganese(II mass metal method mixture molecular molecules Moscow Neorg observed obtained organic oxide parameters phase positions preparation present properties published range rate of solution reaction respectively salts shows similar solid solubility solution solvate solvents specimens spectra stability structure synthesis Table temperature thermal translation translation in Russ tungsten values vibrational X-ray diffraction