Trang 1405
... melt - solid diagram : CrSe , Cr3Se4 , and Cr2Se , [ 5 ] . CrSe melts at 1550 ° C [ 4 ] , and Cr2Se3 melts at 1500 ° C [ 6 ] . With decreasing temperature , the melts of compounds are ordered : for CrSe , at 305 ° C ; for Cr , Se4 , at ...
... melt - solid diagram : CrSe , Cr3Se4 , and Cr2Se , [ 5 ] . CrSe melts at 1550 ° C [ 4 ] , and Cr2Se3 melts at 1500 ° C [ 6 ] . With decreasing temperature , the melts of compounds are ordered : for CrSe , at 305 ° C ; for Cr , Se4 , at ...
Trang 1565
... melt , and the sample melts at 702 ° C , which corresponds to the metastable extension of the sodium metaborate liquidus line . Therefore , in the composition corresponding to sodium diborate , metastable crystallization and melting of ...
... melt , and the sample melts at 702 ° C , which corresponds to the metastable extension of the sodium metaborate liquidus line . Therefore , in the composition corresponding to sodium diborate , metastable crystallization and melting of ...
Trang 1566
... melts congruently at 773 ° C , as in [ 1-3 ] but in contrast to the peritectic melt- ing points of 766 and 765 ° C found in [ 4 , 6 ] . The simi- larity of our results and those in [ 1–3 ] can be attributed to the use of rather bulk ...
... melts congruently at 773 ° C , as in [ 1-3 ] but in contrast to the peritectic melt- ing points of 766 and 765 ° C found in [ 4 , 6 ] . The simi- larity of our results and those in [ 1–3 ] can be attributed to the use of rather bulk ...
Nội dung
Vol 48 No 9 | 1282 |
Simultaneous English language translation of the journal is available from MAIK NaukaInterperiodica Russia | 1446 |
Vol 48 No 11 2003 | 1615 |
28 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid Akad analysis angles anion aqueous atoms band bond lengths calculated cations chelate Chem chemical cm-¹ complexes composition compounds concentration coordination Cr₂Se3 crystal structure Crystallogr curves decomposition decreases diastereomers electron English Translation Copyright enthalpy equilibrium europium europium(III experimental formation formed H₂O hydrogen bonds increases Inorganic Chemistry interaction ions Khim kJ/mol layer ligand lithium MAIK Nauka/Interperiodica melting metal method mixture mol/l Moscow Nauk Neorg octahedra Original Russian Text oxidation oxygen atoms phase diagram Phys Physicochemical plexes properties protons Raman range reaction region Russia Received Russian Academy Russian Journal Russian Text Copyright salt samples single crystals sodium solid solutions solubility solvent sorbent space group spectra spectroscopy spectrum spinel SSUS studied Synthesis Table temperature ternary thermal tion trans transition unit cell unit cell parameters values vibrations water molecules whitlockite X-ray diffraction zirconium