Resistivity , ohm.mm/m 123 Quench 10 % Cr Quench Anneal -P 15 % Cr Quench 16 12 10 Temperature coefficient of resistivity , α - 10-4 FAN 08 Anneal Quench Anneal Quench Anneal a Quench ---- 06 10 20 30 40 50 10 20 30 40 50 10 20 30 40 ...
Resistivity , ohm.mm/m 123 Quench 10 % Cr Quench Anneal -P 15 % Cr Quench 16 12 10 Temperature coefficient of resistivity , α - 10-4 FAN 08 Anneal Quench Anneal Quench Anneal a Quench ---- 06 10 20 30 40 50 10 20 30 40 50 10 20 30 40 ...
Trang 315
... resistivity at elevated temperature in vacuo and in a protective medium Argon cylinder Bulb The hardness of the alloys was measured from the indentation of a pobedite cone at small loads ( 20 kg ) , owing to the brittleness of the ...
... resistivity at elevated temperature in vacuo and in a protective medium Argon cylinder Bulb The hardness of the alloys was measured from the indentation of a pobedite cone at small loads ( 20 kg ) , owing to the brittleness of the ...
Trang 353
... resistivity diagram of titanium - chromium - aluminum alloys The temperature coefficient of resistivity of the alloy with 10 % chromium and 3.33 % aluminum has a negative value , equal to -0.00006 and , in alloys with 3. 33 6.67 ...
... resistivity diagram of titanium - chromium - aluminum alloys The temperature coefficient of resistivity of the alloy with 10 % chromium and 3.33 % aluminum has a negative value , equal to -0.00006 and , in alloys with 3. 33 6.67 ...
Nội dung
The Phase Diagram as an Expression | 4 |
I The Work by N S Kurnakov and | 11 |
REPORTS at the Conference on the Investigation of Phase Dia | 17 |
Bản quyền | |
22 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
a-solid Academy of Sciences alloys alloys containing aluminum annealed atoms B-phase binary systems boundaries calculation cerium chemical compound chromium composition concentration copper corresponding crystallization curves decomposition decreases determined electron elements equations equilibrium diagram eutectic eutectoid Figure formation free energy gold hardness increase Inorganic Chemistry interaction investigated iron aluminide Journal of Inorganic Khim Kornilov lanthanum lattice liquid liquidus magnesium aluminide magnesium silicide manganese maximum melting diagram melting point metallic compounds metallic systems method microstructure Mikheyeva multicomponent systems NiAl nickel number of components number of phases o-phase obtained peritectic phase diagrams platinum properties quaternary system quenched quinary resistivity rhenium silicon six-component solid solution based solid solutions solidus solubility specimens SSSR temperature coefficient ternary system thermal analysis thermodynamic thermoelectromotive force tion titanium carbide tungsten USSR X-ray structural Y₂ Zhur Zhurnal Neorganicheskoi Khimii zinc