... hardness of the alloys of the Ni - Cr - NiAl system on sections passing through 5 , 10 , 15 , and 20 % Cr , showed the following : the hardness of the alloys Ni -- Cr -- NiAl in the state quenched from 1200 ° C , with a Cr content of 5 ...
... hardness of the alloys of the Ni - Cr - NiAl system on sections passing through 5 , 10 , 15 , and 20 % Cr , showed the following : the hardness of the alloys Ni -- Cr -- NiAl in the state quenched from 1200 ° C , with a Cr content of 5 ...
Trang 398
... Hardness at various temperatures , H kg / mm2 K charge , 2 wt . % 20 ° C 300 ° C 400 ° C 500 ° C Titanium 0 210 130 ... hardness of titanium drops by about 50- 60 % from 20 to 500 ° C , while in a titanium alloy with 25 % rhenium , the ...
... Hardness at various temperatures , H kg / mm2 K charge , 2 wt . % 20 ° C 300 ° C 400 ° C 500 ° C Titanium 0 210 130 ... hardness of titanium drops by about 50- 60 % from 20 to 500 ° C , while in a titanium alloy with 25 % rhenium , the ...
Trang 39
... hardness diagram The hardness of the columbium - tungsten alloys was studied in the cast , annealed , and quenched states . The hardness was measured on a Vickers tester , using a pyramid with a load of 10 kg . Table I gives the results ...
... hardness diagram The hardness of the columbium - tungsten alloys was studied in the cast , annealed , and quenched states . The hardness was measured on a Vickers tester , using a pyramid with a load of 10 kg . Table I gives the results ...
Nội dung
The Phase Diagram as an Expression | 4 |
I The Work by N S Kurnakov and | 11 |
REPORTS at the Conference on the Investigation of Phase Dia | 17 |
Bản quyền | |
22 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
a-solid Academy of Sciences alloys alloys containing aluminum annealed atoms B-phase binary systems boundaries calculation cerium chemical compound chromium composition concentration copper corresponding crystallization curves decomposition decreases determined electron elements equations equilibrium diagram eutectic eutectoid Figure formation free energy gold hardness increase Inorganic Chemistry interaction investigated iron aluminide Journal of Inorganic Khim Kornilov lanthanum lattice liquid liquidus magnesium aluminide magnesium silicide manganese maximum melting diagram melting point metallic compounds metallic systems method microstructure Mikheyeva multicomponent systems NiAl nickel number of components number of phases o-phase obtained peritectic phase diagrams platinum properties quaternary system quenched quinary resistivity rhenium silicon six-component solid solution based solid solutions solidus solubility specimens SSSR temperature coefficient ternary system thermal analysis thermodynamic thermoelectromotive force tion titanium carbide tungsten USSR X-ray structural Y₂ Zhur Zhurnal Neorganicheskoi Khimii zinc