... Hydrogen Sorption by Intermetallic Compounds LaNi , and CeCo3 B. P. Tarasov and S. P. Shilkin Institute of New Chemical Problems , Russian Academy of Sciences , plo Chernogolovka , Noginskii raion , Moscow oblast ' , 142432 Russia ...
... Hydrogen Sorption by Intermetallic Compounds LaNi , and CeCo3 B. P. Tarasov and S. P. Shilkin Institute of New Chemical Problems , Russian Academy of Sciences , plo Chernogolovka , Noginskii raion , Moscow oblast ' , 142432 Russia ...
Trang 714
... hydrogen sorption by a 3 - fold excess of ( A ) CeCo3 and ( B ) LaNis ( 1 ) in the absence and ( 2 ) in the presence of 0.5 vol % of CO , ( 3 ) SO2 , and ( 4 ) O2 at ( a ) 293 and ( b ) 373 K. α , % 50 Fig . 2. The curves of. PH2 , MPa ...
... hydrogen sorption by a 3 - fold excess of ( A ) CeCo3 and ( B ) LaNis ( 1 ) in the absence and ( 2 ) in the presence of 0.5 vol % of CO , ( 3 ) SO2 , and ( 4 ) O2 at ( a ) 293 and ( b ) 373 K. α , % 50 Fig . 2. The curves of. PH2 , MPa ...
Trang 715
... hydrogen , the absorption capacity of the intermetal- lides after 150 hydrogen sorption desorption cycles decreased by two times , and drops of water were observed on the reaction chamber walls . The treatment of LaNi , and CeCo , with ...
... hydrogen , the absorption capacity of the intermetal- lides after 150 hydrogen sorption desorption cycles decreased by two times , and drops of water were observed on the reaction chamber walls . The treatment of LaNi , and CeCo , with ...
Nội dung
MAY 30 | 687 |
Synthesis and Properties of Inorganic Compounds | 699 |
Effective Segregation Coefficient of Copper in ZnAs₂ | 707 |
27 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid addition amount analysis anion approximately aqueous atoms bands bismuth bond calculated cations central atom Chem chemical Chemistry cm-¹ complexes components composition compounds concentration considered constant containing coordination copper Copyright corresponding crystal curves decomposition decrease dependence described determined diffraction distribution effect electron elements energy experimental extraction fact formation heating higher hydrogen increase indicates Inorganic intensities interaction ions kcal/mol Khim ligand measured metal method mixture molecules Moscow nature Neorg Note observed obtained occurs organic oxide oxygen parameters peak performed phase podands position possible potassium powder prepared presents properties Publishing range ratio reaction REFERENCES region respectively Russian salts sample Sciences shows similar sodium solid solution space group spectra spectrum stability structure studied synthesis Table temperature thermal tion transition values vibrations weight X-ray