... space group Pna2 . Ten reflections appeared to violate the Pnan space group , which was a rather large number . After refining the whole structure and specifying the major positions of the Ag ( 1,1 ' ) and Ag ( 2,2 ' ) atoms , the final ...
... space group Pna2 . Ten reflections appeared to violate the Pnan space group , which was a rather large number . After refining the whole structure and specifying the major positions of the Ag ( 1,1 ' ) and Ag ( 2,2 ' ) atoms , the final ...
Trang 733
... space group P4332 , Z = 4 , R = 0.021 ( Os – Os , 2.522 Å ; Os - O , 2.091 Å ; Os - Cl , 2.347 Å ; and Os - N , 2.160 Å ) . For L = PPh3 : a = 12.673 Å , b = 13.143 Å , c = 18.330 Å , α = 101.05 ° , B = 91.26 ° , y = 106.04 ° , V = 2871 ...
... space group P4332 , Z = 4 , R = 0.021 ( Os – Os , 2.522 Å ; Os - O , 2.091 Å ; Os - Cl , 2.347 Å ; and Os - N , 2.160 Å ) . For L = PPh3 : a = 12.673 Å , b = 13.143 Å , c = 18.330 Å , α = 101.05 ° , B = 91.26 ° , y = 106.04 ° , V = 2871 ...
Trang 973
... ( space group P4mm , a = 3.867 Å , c = 7.656 Å [ 42 ] ) : -1/2 ( BaO12 ) - ( CuOs ) - [ YOg ] - ( CuOs ) -1/2 ( BaO12 ) . The structure of 124 phase ( for YBa , Cu40g , space group Amm , c = 27.3 Å [ 43 ] ) is described by the scheme [ YO ] ...
... ( space group P4mm , a = 3.867 Å , c = 7.656 Å [ 42 ] ) : -1/2 ( BaO12 ) - ( CuOs ) - [ YOg ] - ( CuOs ) -1/2 ( BaO12 ) . The structure of 124 phase ( for YBa , Cu40g , space group Amm , c = 27.3 Å [ 43 ] ) is described by the scheme [ YO ] ...
Nội dung
Synthesis and Properties of Inorganic Compounds | 695 |
Thermal Dissociation of CaCuO | 703 |
Thermolysis of Antimony Pentoxide Hydrate at the First Stage of the Reduction of SbV to SbIII | 711 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption According acid addition analysis angles anion annealing atoms band bismuth bond calculated carbon cations cell changes chelate Chem chemical Chemistry cm-¹ complexes composition compounds concentration containing coordination Copyright corresponding crystals cubes curves cycles decomposition decrease dependence determined diagram distances effect electron elements energy experimental fluorine formation fragments glass heating increase indicates initial Inorganic intensity ions Journal Khim layers ligand manganese(II materials measured melt metal method mixture molecules Moscow Neorg Note observed obtained occurs oxide oxygen parameters peak peritectic phase positions powder prepared presence properties Publishing range ratio reaction REFERENCES region respectively Russian salt samples Sciences shows solid solutions solubility space group spectra spectrum stability structure studied surface synthesis Table temperature ternary thermal tion Translation unit values vibrations X-ray diffraction