Trang 886
... growth of filamentary Bi2Sг3 - Ca , Cu2O8 + 8 crystals from an amorphous precursor is studied . The factors that control crystal growth kinetics , crystal morphology , structure , and superconducting properties established . A crystal ...
... growth of filamentary Bi2Sг3 - Ca , Cu2O8 + 8 crystals from an amorphous precursor is studied . The factors that control crystal growth kinetics , crystal morphology , structure , and superconducting properties established . A crystal ...
Trang 888
... growth was observed during a 100 - h experiment [ 13 ] . This implies , that the growth kinetics remained unchanged despite the fact that the precursor underwent a fast tran- sition from the amorphous to the crystalline state ...
... growth was observed during a 100 - h experiment [ 13 ] . This implies , that the growth kinetics remained unchanged despite the fact that the precursor underwent a fast tran- sition from the amorphous to the crystalline state ...
Trang 889
... growth was enhanced two to three times . Crystals with maximum dimensions of 5 μm x 100 μm x 10 mm were grown with Al2O3 and ZrO2 doping ( Table 2 ) . Though Al and Zr atoms were not incorporated into the filament lattice , their ...
... growth was enhanced two to three times . Crystals with maximum dimensions of 5 μm x 100 μm x 10 mm were grown with Al2O3 and ZrO2 doping ( Table 2 ) . Though Al and Zr atoms were not incorporated into the filament lattice , their ...
Nội dung
Synthesis and Properties of Inorganic Compounds | 695 |
Thermal Dissociation of CaCuO | 703 |
Thermolysis of Antimony Pentoxide Hydrate at the First Stage of the Reduction of SbV to SbIII | 711 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption According acid addition analysis angles anion annealing atoms band bismuth bond calculated carbon cations cell changes chelate Chem chemical Chemistry cm-¹ complexes composition compounds concentration containing coordination Copyright corresponding crystals cubes curves cycles decomposition decrease dependence determined diagram distances effect electron elements energy experimental fluorine formation fragments glass heating increase indicates initial Inorganic intensity ions Journal Khim layers ligand manganese(II materials measured melt metal method mixture molecules Moscow Neorg Note observed obtained occurs oxide oxygen parameters peak peritectic phase positions powder prepared presence properties Publishing range ratio reaction REFERENCES region respectively Russian salt samples Sciences shows solid solutions solubility space group spectra spectrum stability structure studied surface synthesis Table temperature ternary thermal tion Translation unit values vibrations X-ray diffraction