Russian Journal of Inorganic Chemistry, Tập 41,Trang 683-1012Chemical Society., 1996 |
Từ bên trong sách
Kết quả 1-3 trong 81
Trang 887
Table 1. Composition and properties of filamentary BSCCO crystals depending on the amorphous precursor composition Crystal composition ( cation proportion ) Table 2. Characterization of the precursor ( after annealing ). X - ray ( EDX ) ...
Table 1. Composition and properties of filamentary BSCCO crystals depending on the amorphous precursor composition Crystal composition ( cation proportion ) Table 2. Characterization of the precursor ( after annealing ). X - ray ( EDX ) ...
Trang 950
... composition of the final solution corresponded to the following ratios of atomic concentrations [ Cu ] / ( [ Cu ] + [ Sn ] ) * × 100 % = 0.0 , 0.1 , 0.5 , 1.0 , 3.0 , and 5.0 % . Dried air was a carrier gas . Films 1.5 - μm thick were ...
... composition of the final solution corresponded to the following ratios of atomic concentrations [ Cu ] / ( [ Cu ] + [ Sn ] ) * × 100 % = 0.0 , 0.1 , 0.5 , 1.0 , 3.0 , and 5.0 % . Dried air was a carrier gas . Films 1.5 - μm thick were ...
Trang 960
... composition of samples is given in the table . Transmission 4400 4000 3600 3200 v , cm - 1 2800 2400 2000 Fig . 2. IR absorption spectrum ( v ( OH ) region ) of amor- phous compound for KBr pellet . Chemical composition of samples is ...
... composition of samples is given in the table . Transmission 4400 4000 3600 3200 v , cm - 1 2800 2400 2000 Fig . 2. IR absorption spectrum ( v ( OH ) region ) of amor- phous compound for KBr pellet . Chemical composition of samples is ...
Nội dung
Synthesis and Properties of Inorganic Compounds | 695 |
Thermal Dissociation of CaCuO | 703 |
Thermolysis of Antimony Pentoxide Hydrate at the First Stage of the Reduction of SbV to SbIII | 711 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acetylacetonate acid amorphous analysis anion annealing apatite aqueous solutions atoms band benzotriazole bismuth bond lengths CaO2 carbon cations ceramic chelate chelate cycles Chem chemical cm-¹ complexes composition compounds concentration containing coordination copper corresponding crystals cubes cuprate curves decomposition decrease determined diffraction patterns electron English Translation Copyright enthalpies eutectic experimental films fluorine formation fragments glass glass-formation H₂O Hayka/Interperiodica Publishing Russia heating high-temperature HTSC hydrogen increase Inorg intensity ions Khim kJ/mol lanthanide lanthanum layers ligand liquid manganese(II melt metal method mixture molecules Moscow Neorg obtained Original Russian Text oxide oxygen peak peritectic perovskite phase diagram properties quinaldic acid Raman range ratio reaction region Russia Received Russian Academy Russian Text Copyright samples solid solutions solubility space group spectra spectrum structure studied sulfate superconducting synthesis Table temperature ternary system thermal tion ture vibrations X-ray diffraction X-ray powder diffraction yttrium zinc