Phase Stability and Oxygen Diffusion in RBa2Cu3O6 + x ( R = Y , Nd ) A. P. Mozhaev * , G. N. Mazo * , A. A. Galkin * , and N. V. Khramova ** * Moscow State University , Moscow , 119899 Russia ** Karaganda Metallurgical Institute ...
Phase Stability and Oxygen Diffusion in RBa2Cu3O6 + x ( R = Y , Nd ) A. P. Mozhaev * , G. N. Mazo * , A. A. Galkin * , and N. V. Khramova ** * Moscow State University , Moscow , 119899 Russia ** Karaganda Metallurgical Institute ...
Trang 884
Oxygen diffusion parameters determined for different YBa2Cu306 + x phases Table 4. ... authors [ 6-11 ] made repeated attempts to determine the dependence of oxygen mobility in YBa2Cu306 + on the oxygen concentration in the sam- ple .
Oxygen diffusion parameters determined for different YBa2Cu306 + x phases Table 4. ... authors [ 6-11 ] made repeated attempts to determine the dependence of oxygen mobility in YBa2Cu306 + on the oxygen concentration in the sam- ple .
Trang 994
40000 cm - 1 due to dissolved oxygen . The shoulder disappears upon purg- ing of helium through the melt [ 3 ] . Addition of MnCl2 ( 5 , 7 , 7.5 mol / l ) into NaPO3 melt causes a shift of the absorption edge of NaPO3 to ca.
40000 cm - 1 due to dissolved oxygen . The shoulder disappears upon purg- ing of helium through the melt [ 3 ] . Addition of MnCl2 ( 5 , 7 , 7.5 mol / l ) into NaPO3 melt causes a shift of the absorption edge of NaPO3 to ca.
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
HighTemperature Superconductors | 683 |
Synthesis of Crystalline Bismuth Oxide by Hydrolysis of Bismuth Ethoxide | 695 |
Yankin Yu V Golikov R G Zakharov O A Vikhreva I N Dubrovina and V F Balakirev | 703 |
29 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid addition analysis angles anions atoms band bismuth bond calculated carbon cations cell changes chelate Chem chemical Chemistry cm-¹ complexes components composition compounds concentration containing coordination Copyright corresponding crystals curves cycles decomposition decrease dependence described determined diagram distances effect electron elements energy experimental formation fragments glass heating hydrogen increase indicates initial Inorganic intensity interaction ions Journal Khim layers ligand materials measured melt metal method mixture molecules Moscow Neorg Note observed obtained occurs oxidation oxygen parameters peritectic phase positions powder prepared present properties Publishing range ratio reaction REFERENCES region respectively Russian salt samples Sciences shows similar solid solutions solubility space group spectra spectrum stability structure studied synthesis Table temperature thermal tion transition Translation unit values vibrations X-ray diffraction