Trang 866
... changes are observed upon heating the Nd2O3 + CuO ( 1 : 1 ) mixture consisting of grains 1-3 μm in size to ≈1000 ° C , although some amount of Nd2CuO4 was formed , as the X - ray diffraction data showed . At 1040 ° C , liquid appears ...
... changes are observed upon heating the Nd2O3 + CuO ( 1 : 1 ) mixture consisting of grains 1-3 μm in size to ≈1000 ° C , although some amount of Nd2CuO4 was formed , as the X - ray diffraction data showed . At 1040 ° C , liquid appears ...
Trang 951
... changes as the grain size increases . Films with a relatively small grain size demonstrate a much sharper increase in R , upon cooling . The smoothest R ( T ) dependences for films with a grain size of around 10 nm are fairly well ...
... changes as the grain size increases . Films with a relatively small grain size demonstrate a much sharper increase in R , upon cooling . The smoothest R ( T ) dependences for films with a grain size of around 10 nm are fairly well ...
Trang 991
... changes significantly and contains a broad line with 82.5-2.65 and a line with g1 = 2.85 . These lines undoubtedly correspond to osmium complexes with imidazole . It should be noted that the reaction of trans * - [ Os ( H2O ) Cl ] is ...
... changes significantly and contains a broad line with 82.5-2.65 and a line with g1 = 2.85 . These lines undoubtedly correspond to osmium complexes with imidazole . It should be noted that the reaction of trans * - [ Os ( H2O ) Cl ] is ...
Nội dung
HighTemperature Superconductors | 683 |
Synthesis of Crystalline Bismuth Oxide by Hydrolysis of Bismuth Ethoxide | 695 |
Yankin Yu V Golikov R G Zakharov O A Vikhreva I N Dubrovina and V F Balakirev | 703 |
29 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption according acid addition analysis angles anions atoms band bismuth bond calculated carbon cations cell changes chelate Chem chemical Chemistry cm-¹ complexes components composition compounds concentration containing coordination Copyright corresponding crystals curves cycles decomposition decrease dependence described determined diagram distances effect electron elements energy experimental formation fragments glass heating hydrogen increase indicates initial Inorganic intensity interaction ions Journal Khim layers ligand materials measured melt metal method mixture molecules Moscow Neorg Note observed obtained occurs oxidation oxygen parameters peritectic phase positions powder prepared present properties Publishing range ratio reaction REFERENCES region respectively Russian salt samples Sciences shows similar solid solutions solubility space group spectra spectrum stability structure studied synthesis Table temperature thermal tion transition Translation unit values vibrations X-ray diffraction