... mole % a . A SOKO Er203 , mole % a . A 10.42 0.03 10.46 0.03 5 10.35 ± 0.03 25 10 10.30 0.03 30 15 10.34 0.03 20 10.36 0.03 40 10.43 0.03 10.44 0.03 38395 6-8 ( up to 25 mole % ) the niobium ( II ) oxide disproportionates into metallic ...
... mole % a . A SOKO Er203 , mole % a . A 10.42 0.03 10.46 0.03 5 10.35 ± 0.03 25 10 10.30 0.03 30 15 10.34 0.03 20 10.36 0.03 40 10.43 0.03 10.44 0.03 38395 6-8 ( up to 25 mole % ) the niobium ( II ) oxide disproportionates into metallic ...
Trang 1615
... mole % NiзTe . The solubility based on Ga2Te , is 1.5 mole % and that based on NiзTe , reaches 2 mole at room temperature . The GaTe - NiзTe , section is a quasibinary , eutectic type of system ; the eutectic is at 1043 K and 42 mole ...
... mole % NiзTe . The solubility based on Ga2Te , is 1.5 mole % and that based on NiзTe , reaches 2 mole at room temperature . The GaTe - NiзTe , section is a quasibinary , eutectic type of system ; the eutectic is at 1043 K and 42 mole ...
Trang 1625
... mole % , 909 ° C . The mutual solubility of the components is insignificant and does not exceed 1 mole % NdF3 or 3 mole % FeF2 at the eutectic temperature . Solid solutions based on the high - temperature modification a - GdF3 with a ...
... mole % , 909 ° C . The mutual solubility of the components is insignificant and does not exceed 1 mole % NdF3 or 3 mole % FeF2 at the eutectic temperature . Solid solutions based on the high - temperature modification a - GdF3 with a ...
Nội dung
Inorganic | 919 |
A covertocover translation of Zhurnal Neorganicheskoi Khimii | 1070 |
Journal | 1221 |
Bản quyền | |
10 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid addition analysis anion apparently aqueous atoms bands bismuth bond calculated carried Chem chemical Chemistry chloride complexes components composition compounds concentration constants containing coordination corresponding crystal crystallisation curves decomposition decrease dependence described determined diagram effect electron equilibrium experimental extraction Figure formation formed given gives groups H₂O heating hydrates hydrogen increase indicates infrared spectra Inorg Institute ions Khim lead ligand lines manganese(II mass measured metal method mixture mole molecules Moscow Neorg nitrate observed obtained organic original oxide oxygen parameters phase phosphate points position possible precipitate prepared present pressure properties published pure range ratio reaction Received recorded REFERENCES region respectively Russ salts solid solubility solution solvent specimens spectra spectrum stability structure studied Table takes temperature thermal tion Translated from Zhurnal values vibrations wavenumbers X-ray diffraction Zhur Zhurnal Neorganicheskoi Khimii