Russian Journal of Inorganic Chemistry, Tập 33,Số phát hành 7-12Chemical Society., 1988 |
Từ bên trong sách
Kết quả 1-3 trong 76
Trang 1358
... region extends to 25 mole % Tl2Te and a glassy - crystal- line region from 25 to 40 mole % Tl2Te . With quenching in air the glass formation region is enlarged to 30 mole % T11⁄2Te . -3 = ( 5.10- The density and microhardness values of ...
... region extends to 25 mole % Tl2Te and a glassy - crystal- line region from 25 to 40 mole % Tl2Te . With quenching in air the glass formation region is enlarged to 30 mole % T11⁄2Te . -3 = ( 5.10- The density and microhardness values of ...
Trang 1379
... region . The solidus of the system passes through an isothermal line at 980 K. The phases ɛ , y , and SnTe are observed in the subsolidus part . In the third part of the section the solidus consists of two iso- thermal lines at 900 and ...
... region . The solidus of the system passes through an isothermal line at 980 K. The phases ɛ , y , and SnTe are observed in the subsolidus part . In the third part of the section the solidus consists of two iso- thermal lines at 900 and ...
Trang 1544
... region of the spinel solid solutions has been found using TGA according to the method described earlier . * The rest of the diagram was constructed from the results of a phase analysis of specimens quenched in water from the annealing ...
... region of the spinel solid solutions has been found using TGA according to the method described earlier . * The rest of the diagram was constructed from the results of a phase analysis of specimens quenched in water from the annealing ...
Nội dung
COORDINATION A A Eliseev 927 1635 | 927 |
Journal | 1243 |
The preparation and properties of solid solutions based | 1266 |
Bản quyền | |
7 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1987 Translated absorption acid alkali metal ammonium anion aqueous solutions bands due bond calculated cation Chem chemical Chemistry chloride cm-¹ cm¯¹ cm¹ cobalt cobalt(II components composition concentration constant containing copper(II corresponding crystallisation crystals curves decrease determined electronic endothermic equilibrium diagram ethanol europium eutectic experimental Figure formed H₂O heating hydrated hydrogen hydroxide increase indicate infrared spectra Inorg Inorganic interaction ions iron(III isomerisation Khim L₁ lanthanide ligand mass loss melting method mixture mole Moscow Nauk SSSR Neorg nickel nickel(II nitrate nitrogen obtained octahedral oxide oxygen atoms parameters phosphate platinum(II potassium precipitate present proton ratio reaction rhenium Russ Russ.J Russ.J.Inorg salt sodium solid solutions solubility specimens spectrum structure studied sulphate synthesis Table ternary thermal analysis thermal decomposition thiourea tion Translated from Zhurnal values vibrations water molecules wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhur.Neorg.Khim Zhurnal Neorganicheskoi Khimii