The data obtained are used to develop a procedure for preparing ceramic and thick - film samples , free of impurities and with the superconducting transition occurring at T > 100 K. Using formates considerably simplifies the preparation ...
The data obtained are used to develop a procedure for preparing ceramic and thick - film samples , free of impurities and with the superconducting transition occurring at T > 100 K. Using formates considerably simplifies the preparation ...
Trang 1028
We failed to prepare the pure ( 2223 ) phase without partially replacing bismuth with lead . In this case , varying the preparation conditions in rather wide ranges did not succeed . 3 The described process for preparing 3 Bi2 - Pb ...
We failed to prepare the pure ( 2223 ) phase without partially replacing bismuth with lead . In this case , varying the preparation conditions in rather wide ranges did not succeed . 3 The described process for preparing 3 Bi2 - Pb ...
Trang 1241
Preparation , Structure , and Thermal Properties of Na [ Pd ( C202 ) 2 ] . ... Russia Received December 9 , 1994 = Abstract – The Na2 [ Pd ( C2O4 ) 2 ] · 2H20 salt is prepared from palladium hydroxide by an original procedure .
Preparation , Structure , and Thermal Properties of Na [ Pd ( C202 ) 2 ] . ... Russia Received December 9 , 1994 = Abstract – The Na2 [ Pd ( C2O4 ) 2 ] · 2H20 salt is prepared from palladium hydroxide by an original procedure .
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Vol 40 No 7 | 1021 |
Synthesis of LaCuNi 025+ 8 from Carboxylates | 1030 |
A A Andreev M F Bulanyi S A Golikov and L A Mozharovskii | 1039 |
Bản quyền | |
7 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption Academy of Sciences according acid activity addition analysis angles anion aqueous atoms bands bond calculated cation cell changes Chem chemical Chemistry complexes composition compounds concentration constants containing coordination copper Copyright corresponding crystals curves decomposition decrease dependence described determined distances effect electron energy equilibrium experimental extraction fact fluoride formation groups heating hydrogen increase indicates initial Inorganic Institute intensity interaction ions Khim ligand lines melt metal method mixture molecules Moscow Neorg Note observed obtained occurs oxide oxygen parameters phase position powder prepared presented pressure properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples shift shows similar sodium solid solubility solutions spectra spectrum stability structure studied synthesis Table temperature tetrahedral thermal tion Translation values vibrations X-ray diffraction