Trang 248
... melts with M20 : P2O5 ratios ( M = = Li , Na , or K ) were prepared by melting MPO3 , M4P2O7 , and M2P4O11 in various molar ratios . The last was obtained by melting a 1 : 1 mixture of MPO3 and ( NH4 ) 2HPO4 at 700 ° C . The amount of ...
... melts with M20 : P2O5 ratios ( M = = Li , Na , or K ) were prepared by melting MPO3 , M4P2O7 , and M2P4O11 in various molar ratios . The last was obtained by melting a 1 : 1 mixture of MPO3 and ( NH4 ) 2HPO4 at 700 ° C . The amount of ...
Trang 249
... melting point determinations showed that all the compounds are very refractory and melt with decomposi- tion . Table 1. Some crystallographic data for the compounds obtained . Compound a ( A ) e ( A ) VIA ) ng LiZr2 ( PO . ) 3 123 np ...
... melting point determinations showed that all the compounds are very refractory and melt with decomposi- tion . Table 1. Some crystallographic data for the compounds obtained . Compound a ( A ) e ( A ) VIA ) ng LiZr2 ( PO . ) 3 123 np ...
Trang 308
... melting point > 1470 K were fused in an arc furnace . A combined apparatus was used to determine the melting points ( m.p. > 2000 K ) of the refractory materials . 10 The uncertainty is ± 10 K. The XRD and MSA procedures were similar to ...
... melting point > 1470 K were fused in an arc furnace . A combined apparatus was used to determine the melting points ( m.p. > 2000 K ) of the refractory materials . 10 The uncertainty is ± 10 K. The XRD and MSA procedures were similar to ...
Nội dung
CONTENTS | 1 |
Transformations in the LaCuH system | 10 |
The preparation and electrical properties of various | 17 |
Bản quyền | |
4 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1986 Translated absorption acid acrolein Akad alkali metal anion bands bond calculated cation Chem Chemistry chloride chromium(III cm-¹ cm¹ cobalt(II complex formation components composition compounds concentration containing coordination copper(II corresponding crystal crystallisation curves decrease determined electron endothermic ethanol experimental extraction Figure fluoride formed groups H₂O heating hydrate hydrogen increase infrared spectra Inorg Inorganic ionic ions iron(III isotherms Khim Khimiya lanthanide lanthanum lattice ligand lithium mass melting method mixture mole Moscow Nauk SSSR Neorg nickel(II nitrogen obtained oxide parameters phosphate physicochemical plexes potassium precipitate present protons range reaction rhodium(III rubidium Russ Russ.J salt shows sodium solid phase solid solutions solubility specimens spectrum stability constants structure studied sulphate synthesis temperature ternary thermal analysis thermal decomposition Thio tion titration Translated from Zhurnal values vibrations water molecules wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhur.Neorg Zhurnal Neorganicheskoi Khimii