... crystals Bi1.85Sr1.85 Ca0.87 Cu2.00Ox and Bi2.53Sг1.90 Ca0.90Cu2.000 , of 5 x 5 x 0.1 mm on average and with T , = 87 K , are prepared . The ( 2223 ) phase is found as thin layers in the crystals of the ( 2212 ) phase . 1 Conditions for ...
... crystals Bi1.85Sr1.85 Ca0.87 Cu2.00Ox and Bi2.53Sг1.90 Ca0.90Cu2.000 , of 5 x 5 x 0.1 mm on average and with T , = 87 K , are prepared . The ( 2223 ) phase is found as thin layers in the crystals of the ( 2212 ) phase . 1 Conditions for ...
Trang
... crystals ( which were about 1 mm in size or larger ) were separated mechanically using an MBS - 1 microscope . It ... crystals at various current densities Jacross the sample : ( 1 ) 3 and ( 2 ) 150 A / cm2 . Crystallization products ...
... crystals ( which were about 1 mm in size or larger ) were separated mechanically using an MBS - 1 microscope . It ... crystals at various current densities Jacross the sample : ( 1 ) 3 and ( 2 ) 150 A / cm2 . Crystallization products ...
Trang 372
... crystals were maintained in the reaction vessel at -20 , -10 , and 20 ° C until they completely decomposed . They were then investigated at room temperature by the X - ray powder diffraction method and IR and Raman spectroscopy , and ...
... crystals were maintained in the reaction vessel at -20 , -10 , and 20 ° C until they completely decomposed . They were then investigated at room temperature by the X - ray powder diffraction method and IR and Raman spectroscopy , and ...
Nội dung
Interaction of Lithium Borohydride with Lithium Hydroxide | 6 |
Synthesis and Thermal Decomposition of the Aluminum Hydroxide Intercalation Compounds | 18 |
Electrical Conductivity and Reduction Thermodynamics of Indium Oxide and Solid Solutions Based on | 35 |
Bản quyền | |
43 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption bands acetylacetone acid Akad alkaline ammonia analysis anion aqueous solutions atoms bond calculated cations Chem chemical Chemistry chloride cm-¹ cobalt(II complexes composition concentration COORDINATION COMPOUNDS copper(II crystal curves decomposition determined electron English Translation Copyright equation equilibrium eutectic experimental formation gallium(III groups H₂O Hayka/Interperiodica Publishing Russia heating hydrated hydrogen Inorg Inorganic interaction ionic strength ions Khim lanthanide LiCl ligand Ln(III MAHK Hayka/Interperiodica Publishing melting metal method mixture mol/dm³ mol/l molecule Moscow NaCl Nauk SSSR Neorg nitrate obtained orbital Original Russian Text oxide oxygen perchlorate phase diagram plexes pyridine ratio reaction reagent region Russia Russia Received Russian Academy Russian Text Copyright ruthenium(III salts samples sodium solid solutions solu solubility solvent sorbent sorption spectra spectrum stability constants structure studied synthesis Table tautomer Tb(III temperature ternary thermal thermolysis tion unit-cell parameters values vibrations X-ray diffraction X-ray powder diffraction