... crystals Bi1.85Sr1.85 Ca0.87 Cu2.00Ox and Bi2.53 Sr1.90 Ca0.90 Cu2.000 of 5 x 5 x 0.1 mm on average and with T , = 87 K , are prepared . The ( 2223 ) phase is found as thin layers in the crystals of the ( 2212 ) phase . Conditions for ...
... crystals Bi1.85Sr1.85 Ca0.87 Cu2.00Ox and Bi2.53 Sr1.90 Ca0.90 Cu2.000 of 5 x 5 x 0.1 mm on average and with T , = 87 K , are prepared . The ( 2223 ) phase is found as thin layers in the crystals of the ( 2212 ) phase . Conditions for ...
Trang 4
... crystals ( which were about 1 mm in size or larger ) were separated mechanically using an MBS - 1 microscope . It ... crystals at various current densities Jacross the sample : ( 1 ) 3 and ( 2 ) 150 A / cm2 . Crystallization ...
... crystals ( which were about 1 mm in size or larger ) were separated mechanically using an MBS - 1 microscope . It ... crystals at various current densities Jacross the sample : ( 1 ) 3 and ( 2 ) 150 A / cm2 . Crystallization ...
Trang 5
... crystals was 0.1-0.3 wt % . The superconducting properties of the crystals were studied by measuring the temperature dependence of the electrical resistivity in a temperature range 4.2 to 300 K using the four - probe technique . The ...
... crystals was 0.1-0.3 wt % . The superconducting properties of the crystals were studied by measuring the temperature dependence of the electrical resistivity in a temperature range 4.2 to 300 K using the four - probe technique . The ...
Nội dung
HighTemperature Superconductors | 3 |
Interaction of Lithium Borohydride with Lithium Hydroxide | 12 |
The Synthesis and Properties | 27 |
Bản quyền | |
47 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption bands acetylacetone Akad analysis anion aqueous solutions atoms binary bismuth bond calcd calculated cations Chem chemical chloride cm-¹ composition concentration COORDINATION COMPOUNDS copper(II corresponding crystals curves decomposition determined electronic English Translation Copyright equation equilibrium eutectic experimental GeSe₂ groups H₂O Hayka/Interperiodica Publishing Russia heating hydrated hydrochloric acid hydrogen Inorg interaction ions Khim lanthanide ligand Ln(III MAHK Hayka/Interperiodica Publishing melting metal method mixture MnMoO4 mol/l molecule molybdates Moscow Nauk SSSR Neorg nickel(II nitrate obtained Original Russian Text oxide oxygen particles perchlorate phase diagram physicochemical plexes precipitate properties pyridine rare-earth ratio reaction reagent region Russia Received Russian Academy Russian Text Copyright salts samples sodium solid solutions solu solubility solvent sorbent spectra spectrum stability constants structure studied superconducting synthesis Table tautomer temperature ternary thermal thermolysis tion unit-cell parameters values vibrations X-ray diffraction X-ray powder diffraction yttrium