Their unit cell parameters are a = 0.43887 ( 2 ) nm , b = 0.70076 ( 3 ) nm , c = 0.76682 ( 3 ) nm and a = 0.4418 ( 1 ) nm , b = 0.7026 ( 2 ) nm , c = 0.7637 ( 2 ) nm , respectively . YPd0.32Ga1.68 is of the Caln2 structural type , space ...
Their unit cell parameters are a = 0.43887 ( 2 ) nm , b = 0.70076 ( 3 ) nm , c = 0.76682 ( 3 ) nm and a = 0.4418 ( 1 ) nm , b = 0.7026 ( 2 ) nm , c = 0.7637 ( 2 ) nm , respectively . YPd0.32Ga1.68 is of the Caln2 structural type , space ...
Trang 592
The unit cell parameters of the major phase with the CaCuO2 structure were refined tentatively by the least- squares fit based on the reflections in the 20 ° < 20 < 70 ° range and finally using the DWBS - 9411 program .
The unit cell parameters of the major phase with the CaCuO2 structure were refined tentatively by the least- squares fit based on the reflections in the 20 ° < 20 < 70 ° range and finally using the DWBS - 9411 program .
Trang 828
In this case , the unit cell parameters of phase ( 123 ) ( Table 1 ; series II , samples 1 , 2 , 4 , 5 ) are close to those of the YBa2Cu3.107-8 solid solution ( Table 3 ) . An investigation of copper solubility gives similar results ...
In this case , the unit cell parameters of phase ( 123 ) ( Table 1 ; series II , samples 1 , 2 , 4 , 5 ) are close to those of the YBa2Cu3.107-8 solid solution ( Table 3 ) . An investigation of copper solubility gives similar results ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Synthesis and Properties of Inorganic Compounds | 465 |
Titanium Germanate | 472 |
Coordination Compounds | 479 |
Bản quyền | |
27 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption acid addition analysis angle anion aqueous atoms band bond calculated cation changes charge Chem chemical Chemistry cluster cm-¹ complex composition compounds concentration constant containing coordination Copyright corresponding crystal curves decomposition decrease dependence determined distances effect electron energy exchange experimental extraction field formation fragments heating hydride hydrogen increase initial Inorganic intensity interaction ions Journal Khim ligand measured melting metal method mixture mol/l molecules Moscow Neorg Note observed obtained occurs oxidation oxygen parameters patterns peritectic phase plane polyhedra position powder prepared processes properties Publishing range ratio reaction REFERENCES region respectively Russian salts samples Sciences shift showed similar solid solid solutions solubility solution space group spectra spectrum stability structure studied suggested synthesis Table temperature thermal tion Translation unit cell values X-ray diffraction