... values of n for the pure component , and is ( 119 ± 10 ) × 10-6 . This agrees with the value of nexpt for the quantity of GeCl4 in excess , indicating that the components react to form the 1 : 1 complex . Thus the complex GeC14.bipy can ...
... values of n for the pure component , and is ( 119 ± 10 ) × 10-6 . This agrees with the value of nexpt for the quantity of GeCl4 in excess , indicating that the components react to form the 1 : 1 complex . Thus the complex GeC14.bipy can ...
Trang 1730
... values for the density Pexp 44202 and 4540 kg m − 3 4 give Z = 2 , from which Pcalc 4635 ( 4 ) kg m3 . The indexing of the X - ray diffraction pattern of the powdered crystals ( FR552 camera , Cu Kα , radiation ) is given in Table 1 ...
... values for the density Pexp 44202 and 4540 kg m − 3 4 give Z = 2 , from which Pcalc 4635 ( 4 ) kg m3 . The indexing of the X - ray diffraction pattern of the powdered crystals ( FR552 camera , Cu Kα , radiation ) is given in Table 1 ...
Trang 1775
... values of the logarithms of the stability constants are the average values from 6-8 experiments . The uncertainty was determined as the mean - square deviation from the mean value with allowance for the Student coefficient for a ...
... values of the logarithms of the stability constants are the average values from 6-8 experiments . The uncertainty was determined as the mean - square deviation from the mean value with allowance for the Student coefficient for a ...
Nội dung
Journal of | 1243 |
Higher oxides of praseodymium and neodymium | 1250 |
Point defects in gadolinium gallium garnet | 1256 |
Bản quyền | |
5 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1987 Translated absorption acid anion aqueous solution bond calculated cation Chem chemical Chemistry chloride chromium(VI cm-¹ cm¯¹ cm¹ complex formation components composition compounds concentration constant containing coordination copper(II corresponding crystallisation crystals curves decrease density determined electronic endothermic equilibrium diagram europium eutectic experimental extraction Figure fluorides fluorine formed H₂O heating hydrated hydrogen hydrogen bonds hydroxide i.r. spectra increase indicates infrared spectra Inorg Inorganic ionic ions iron(III Khim Khimiya lanthanide lanthanum lattice ligand melts metal method mixture mole Moscow Nauk SSSR Neorg nickel(II nitrate nitrogen obtained oxide palladium(II parameters phosphates platinum(II potassium precipitate present proton Raman ratio reaction reagent Russ ruthenium salts shows sodium solid phase solid solutions solubility specimens spectra spectrum structure studied sulphate sulphur synthesis thermal analysis thermal decomposition tion Translated from Zhurnal values vibrations water molecules wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhurnal Neorganicheskoi Khimii