... eutectic between SnTe and Co , Sn , Te , crystallises at 12 mole % Co and 1020 K. The second eutectic point is at 74 mole % Co and 1230 K. The a solid solution region extends to 5 mole % Co at room temperature and remains almost the ...
... eutectic between SnTe and Co , Sn , Te , crystallises at 12 mole % Co and 1020 K. The second eutectic point is at 74 mole % Co and 1230 K. The a solid solution region extends to 5 mole % Co at room temperature and remains almost the ...
Trang 1398
... Eutectic transformations occur at KBiCl4 30 mole % , ( 1862 ) ° C and at KBiCl4 80 mole % , ( 1302 ) ° C ( Fig.a ) . The NaBiCl4 - K3BiCl , Quasibinary System In this system there is the congruently melting compound 3NaBiCl4.7K3BiCl ...
... Eutectic transformations occur at KBiCl4 30 mole % , ( 1862 ) ° C and at KBiCl4 80 mole % , ( 1302 ) ° C ( Fig.a ) . The NaBiCl4 - K3BiCl , Quasibinary System In this system there is the congruently melting compound 3NaBiCl4.7K3BiCl ...
Trang 1548
The LiMgCr ( MoO4 ) 3 – Li3Cr ( M0O4 ) 3 system is eutectic . The eutectic is at Li3Cr ( M0O4 ) 3 90 mole % , 770 ° C ( Fig.b ) . The MgMoO4 - LiCr ( MoO4 ) 2 and Li2Mg2 ( M0O4 ) 3 — Cr2 ( M0O4 ) 3 sections are [ each ] divided by the ...
The LiMgCr ( MoO4 ) 3 – Li3Cr ( M0O4 ) 3 system is eutectic . The eutectic is at Li3Cr ( M0O4 ) 3 90 mole % , 770 ° C ( Fig.b ) . The MgMoO4 - LiCr ( MoO4 ) 2 and Li2Mg2 ( M0O4 ) 3 — Cr2 ( M0O4 ) 3 sections are [ each ] divided by the ...
Nội dung
Journal of | 1243 |
Higher oxides of praseodymium and neodymium | 1250 |
Point defects in gadolinium gallium garnet | 1256 |
Bản quyền | |
5 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1987 Translated absorption acid anion aqueous solution bond calculated cation Chem chemical Chemistry chloride chromium(VI cm-¹ cm¯¹ cm¹ complex formation components composition compounds concentration constant containing coordination copper(II corresponding crystallisation crystals curves decrease density determined electronic endothermic equilibrium diagram europium eutectic experimental extraction Figure fluorides fluorine formed H₂O heating hydrated hydrogen hydrogen bonds hydroxide i.r. spectra increase indicates infrared spectra Inorg Inorganic ionic ions iron(III Khim Khimiya lanthanide lanthanum lattice ligand melts metal method mixture mole Moscow Nauk SSSR Neorg nickel(II nitrate nitrogen obtained oxide palladium(II parameters phosphates platinum(II potassium precipitate present proton Raman ratio reaction reagent Russ ruthenium salts shows sodium solid phase solid solutions solubility specimens spectra spectrum structure studied sulphate sulphur synthesis thermal analysis thermal decomposition tion Translated from Zhurnal values vibrations water molecules wavenumbers X-ray diffraction X-ray diffraction patterns Zhur Zhurnal Neorganicheskoi Khimii