Trang 880
... precipitate was treated as described in the previous case . D = 0.01 -0.03 mm . Found , wt % : ( NH4 ) 2O , 15.0 ; Li2O , 13.9 ; P2O5 , 61.8 ( P1 , 0.5 ; P2 , 1.3 ; P3 , 98.2 ) ; H2O , 9.3 . Calculated for ( NH4 ) 2L13P3010 · 2H2O , wt ...
... precipitate was treated as described in the previous case . D = 0.01 -0.03 mm . Found , wt % : ( NH4 ) 2O , 15.0 ; Li2O , 13.9 ; P2O5 , 61.8 ( P1 , 0.5 ; P2 , 1.3 ; P3 , 98.2 ) ; H2O , 9.3 . Calculated for ( NH4 ) 2L13P3010 · 2H2O , wt ...
Trang 883
... precipitate ( OP - 205 pH meter ) changes from 8.1 to 6.9 in the first series and from 7.2 to 8.2 in the second series . The pre- vailing anionic form in the solution at these pH values is P30 % with insignificant amounts of the H ...
... precipitate ( OP - 205 pH meter ) changes from 8.1 to 6.9 in the first series and from 7.2 to 8.2 in the second series . The pre- vailing anionic form in the solution at these pH values is P30 % with insignificant amounts of the H ...
Trang 886
... precipitate spontaneously , in contrast to what was described in the literature ; instead K2CdP207 4H2O crystallized over a wide range of the system in the form of elongated acicular crystals or irregularly shaped thin plates . Table 1 ...
... precipitate spontaneously , in contrast to what was described in the literature ; instead K2CdP207 4H2O crystallized over a wide range of the system in the form of elongated acicular crystals or irregularly shaped thin plates . Table 1 ...
Nội dung
Vol 38 No 3 | 363 |
StandardFree ElectronProbe Microanalysis of Submicron Films of HTSC Oxides and Semiconductors | 373 |
Phase Formation in Zirconium Sulfate Solutions in the Presence of Sodium Fluoride | 379 |
Bản quyền | |
27 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1993 by Interperiodica 1993 by Zhurnal absorption band acid Akad alkali metal analysis anion aqueous solutions atoms binary bond lengths calculated cations Chem chemical chromium(III cm-¹ Co² complexes composition compounds concentration coordination COORDINATION COMPOUNDS coordination sphere copper(II corresponding curves decomposition decrease determined diffraction patterns electron English Translation Copyright equilibrium experimental films fluorine formation H₂O hydrolysis increase interaction ionic ions Khim kinetic kJ/mol lattice layer ligand melting method mixture mol/l molecules Moscow Nauk SSSR Neorg obtained Original Russian Edition oxide oxygen oxygen atoms parameters phosphates Phys plexes polyhedra polyphosphate potassium precipitate pyridine ratio reaction Russia Received Russian Academy Russian Edition Copyright ruthenium(III salts samples solid phase solid solutions solu solubility solvent space group spectra spectrum stability stoichiometry structural type studied synthesis Table temperature ternary thermal tion values vapor vibrations X-ray diffraction Zhurnal Neorganicheskoi Khimii