Russian Journal of Inorganic Chemistry, Tập 45British Library Lending Division with the cooperation of the Royal Society of Chemistry, 2000 |
Từ bên trong sách
Kết quả 1-3 trong 80
Trang S-93
... temperature to become Pa ' : Pb : Pc 1000 : 1 : 1.1 at 80 K. Hall effect studies with varied magnetic field orien- tations showed that the Hall constant was anisotropic . However , neither temperature curves for R and u nor the extents ...
... temperature to become Pa ' : Pb : Pc 1000 : 1 : 1.1 at 80 K. Hall effect studies with varied magnetic field orien- tations showed that the Hall constant was anisotropic . However , neither temperature curves for R and u nor the extents ...
Trang S-94
... temperature curves for oriented ZnAs2 specimens [ 136 ] . ( 1 ) Tellurium - doped specimens . α , mV / K Δα , mV / K 5r ZnAs2 4 1.2 3 4 2 1.1 2 아 3 150 1.0 100 150 200 250 300 350 T , K Fig . 18. Seebeck coefficient vs. temperature for ...
... temperature curves for oriented ZnAs2 specimens [ 136 ] . ( 1 ) Tellurium - doped specimens . α , mV / K Δα , mV / K 5r ZnAs2 4 1.2 3 4 2 1.1 2 아 3 150 1.0 100 150 200 250 300 350 T , K Fig . 18. Seebeck coefficient vs. temperature for ...
Trang S-95
... temperature sensitivity about ten times as high and a voltage - wattage sensitivity about twice as high as the pertinent values of the CdSb device . The higher thermal conductivity of ZnAs2 provides for about a six- fold decrease in the ...
... temperature sensitivity about ten times as high and a voltage - wattage sensitivity about twice as high as the pertinent values of the CdSb device . The higher thermal conductivity of ZnAs2 provides for about a six- fold decrease in the ...
Nội dung
Vol 45 Suppl 1 | S-2 |
Effect of Defects on Electronic Structure Chemical Bonding | S-3 |
Conclusions | S-30 |
Bản quyền | |
4 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
addition analysis angle anions atoms band bond calculated cations characteristics characterized Chem chemical Chemistry close complexes composition compounds concentration conductivity considerable considered containing coordination corresponding crystal curves decrease defects density dependence described determined diffusion direct distance distribution domain effect electron elements energy example existence faces fluorides formation given groups impurity increase influence Inorganic interactions interatomic involved ionic Journal lattice layer ligand magnetic Mater melting metal method molecules nature Neorg nitride Note observed occur overlap oxide oxygen packing parameters phase Phys Physics polyhedron positions possible processes properties radii range reaction region respectively rule Russian shift shows similar single solid solutions space space group spectra sphere stability structure studied surface Table temperature tion topological trans transition unit vacancies values VD polyhedra