As a rule , the dislocation density in bulk metal single crystals averages 106 to 109 cm - 2 . The equilibrium density is far lower , to the point where it may decrease to unit dislocations , which often occurs in semiconductor single ...
As a rule , the dislocation density in bulk metal single crystals averages 106 to 109 cm - 2 . The equilibrium density is far lower , to the point where it may decrease to unit dislocations , which often occurs in semiconductor single ...
Trang S-67
( 5 ) In the absence of large - angle boundaries , the higher the temperature and the lower the stress , the larger the increment in the high - temperature creep resistance of metal single crystals . The reason for this is the exclusion ...
( 5 ) In the absence of large - angle boundaries , the higher the temperature and the lower the stress , the larger the increment in the high - temperature creep resistance of metal single crystals . The reason for this is the exclusion ...
Trang S-76
The Bridgman - Stockdiameter of drops of molten tungsten that feed the bath barger technique has been applied to grow multicompoat the tip of the growing single crystal . Even higher effi- nent mixed crystals of the iron - cobalt ...
The Bridgman - Stockdiameter of drops of molten tungsten that feed the bath barger technique has been applied to grow multicompoat the tip of the growing single crystal . Even higher effi- nent mixed crystals of the iron - cobalt ...
Nội dung mọi người đang nói đến - Viết bài đánh giá
Chúng tôi không t́m thấy bài đánh giá nào ở các vị trí thông thường.
Nội dung
Effect of Defects on Electronic Structure Chemical Bonding | S-3 |
Contents | S-16 |
Conclusions | S-30 |
Bản quyền | |
4 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
addition analysis angle anions atoms average band bond calculated cations characteristics characterized Chem chemical Chemistry close complexes composition compounds concentration conductivity considerable considered containing coordination corresponding crystal curves decrease defects density dependence described determined diffusion direct distance distribution domain effect electron elements energy example existence faces fluorides formation given groups impurity increase influence Inorganic interactions interatomic involved ionic Journal lattice layer ligand magnetic materials melting metal method molecules nature nitride Note observed occur overlap oxide oxygen packing parameters phase Phys Physics polyhedron positions possible processes properties radii range reaction region respectively rule Russian shift shows similar single solid solutions space space group spectra sphere stability structure studied surface Table temperature tion topological trans transition unit vacancies values VD polyhedra
Thông tin thư mục
| Tiêu đề | Russian Journal of Inorganic Chemistry, Tập 45 |
| Cộng tác viên | British Library. Lending Division, Akademii︠a︡ nauk SSSR., Royal Society of Chemistry (Great Britain), Chemical Society (Great Britain) |
| Nhà xuất bản | British Library Lending Division with the cooperation of the Royal Society of Chemistry, 2000 |
| Nguyên bản từ | Đại học Michigan |
| Đă được số hóa | 9 Tháng 4 2010 |
| Xuất lời trích dẫn | BiBTeX EndNote RefMan |