Russian Journal of Inorganic Chemistry, Tập 45British Library Lending Division with the cooperation of the Royal Society of Chemistry, 2000 |
Từ bên trong sách
Kết quả 1-3 trong 35
Trang S-10
... band . The states constituting this band have a spheri- cally symmetric shape of molecular - type s orbitals ( Fig . 8 ) . The second , partially filled , band of vacancy states localized near the bottom of the band gap involves the ...
... band . The states constituting this band have a spheri- cally symmetric shape of molecular - type s orbitals ( Fig . 8 ) . The second , partially filled , band of vacancy states localized near the bottom of the band gap involves the ...
Trang S-91
... bands are difficult in principle . Until recently , no uni- fied notion about the band structure of CdAs2 existed . Experimental evidence was inconsistent . There was no consensus regarding the positions of points at which absolute ...
... bands are difficult in principle . Until recently , no uni- fied notion about the band structure of CdAs2 existed . Experimental evidence was inconsistent . There was no consensus regarding the positions of points at which absolute ...
Trang S-99
... band of an unknown nature with a peak at hv≈ 0.965 eV and a half - width of ca. 25 meV is characteristic of the PL spectra at 78 K. This band is most well - pronounced in type 2 spectra . Because the absorption edge of ZnAs , in ...
... band of an unknown nature with a peak at hv≈ 0.965 eV and a half - width of ca. 25 meV is characteristic of the PL spectra at 78 K. This band is most well - pronounced in type 2 spectra . Because the absorption edge of ZnAs , in ...
Nội dung
Vol 45 Suppl 1 | S-2 |
Effect of Defects on Electronic Structure Chemical Bonding | S-3 |
Conclusions | S-30 |
Bản quyền | |
4 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
addition analysis angle anions atoms band bond calculated cations characteristics characterized Chem chemical Chemistry close complexes composition compounds concentration conductivity considerable considered containing coordination corresponding crystal curves decrease defects density dependence described determined diffusion direct distance distribution domain effect electron elements energy example existence faces fluorides formation given groups impurity increase influence Inorganic interactions interatomic involved ionic Journal lattice layer ligand magnetic Mater melting metal method molecules nature Neorg nitride Note observed occur overlap oxide oxygen packing parameters phase Phys Physics polyhedron positions possible processes properties radii range reaction region respectively rule Russian shift shows similar single solid solutions space space group spectra sphere stability structure studied surface Table temperature tion topological trans transition unit vacancies values VD polyhedra