... mole % 2CdTe , the ingots had a slight porosity , which was a maximum at 50 mole % 2CdTe . The X - ray diffraction patterns of the alloys in the range 30-95 mole % 2CdTe showed two systems of reflec- tions , indicating their heterophase ...
... mole % 2CdTe , the ingots had a slight porosity , which was a maximum at 50 mole % 2CdTe . The X - ray diffraction patterns of the alloys in the range 30-95 mole % 2CdTe showed two systems of reflec- tions , indicating their heterophase ...
Trang 1379
... mole % ZnSe two microhardnesses are observed - 250 and 223 kgf mm 2. When the ZnSe concentration is increased further the microhardness rises from 223 kgf mm for the specimen with 7.5 mole % ZnSe to 290 kgf mm - 2 for that with 16 mole ...
... mole % ZnSe two microhardnesses are observed - 250 and 223 kgf mm 2. When the ZnSe concentration is increased further the microhardness rises from 223 kgf mm for the specimen with 7.5 mole % ZnSe to 290 kgf mm - 2 for that with 16 mole ...
Trang 1843
... mole % of the other component at the Sb2S3 side , ~ 6 mole % at the Sb2Se , side . The solid solu- tion regions extend to 1.5 mole % at 450 ° C at the CdS and CdSe sides . Hence specimens with 0.25 , 0.5 , and 3 1 mole % are single ...
... mole % of the other component at the Sb2S3 side , ~ 6 mole % at the Sb2Se , side . The solid solu- tion regions extend to 1.5 mole % at 450 ° C at the CdS and CdSe sides . Hence specimens with 0.25 , 0.5 , and 3 1 mole % are single ...
Nội dung
COORDINATION coordination compounds in solution | 943 |
Interaction of vanadiumV oxide with holmium | 953 |
Influence of sulphur dioxide on the chlorination | 962 |
Bản quyền | |
1 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1977 Translated absorption bands acid Akad analysis anions aqueous solutions atom bond caesium calculated cations Chem chemical Chemistry chloride cm-¹ cm¹ coefficients complex formation composition compounds concentration coordination copper(II corresponding crystallisation crystals curve decrease density determined dissociation endothermic enthalpies equation equilibrium diagram erbium eutectic experimental extraction Figure fluoride formed H₂O heating hydrated hydrazine hydrogen increase indium infrared infrared spectra Inorg Inorganic ionic ions iron(II isotherms kcal Khim Khimiya ligand lithium melts metal method mixture molar mole molecules Moscow Nauk SSSR neodymium Neorg nitrate obtained oxide per-rhenate platinum(II plexes potassium precipitate pyridine range ratio reaction reagent rubidium Russ salts shows sodium solid phase solid solutions solubility solvation specimens spectrum stability constants structure studied Table temperature ternary tion Translated from Zhurnal Translated into Russian values vanadium vanadium(V vibrations wavenumbers X-ray diffraction Zhur Zhurnal Neorganicheskoi Khimii