... thermal expansion coefficients between 90 and 650 K were determined by X - ray diffraction . The thermal expansion of CuGa3Se , is anisotropic , and the thermal - expansion coefficient along the c axis is lower than that along the a ...
... thermal expansion coefficients between 90 and 650 K were determined by X - ray diffraction . The thermal expansion of CuGa3Se , is anisotropic , and the thermal - expansion coefficient along the c axis is lower than that along the a ...
Trang 1452
... Thermal expansion coefficients ankl of CuGa3Ses versus cos2 at ( 1 ) 150 , ( 2 ) 300 , ( 3 ) 450 , and ( 4 ) 600 K. α × 106 , Κ - 1 15- 10 5 0 ( a ) -5- P ( b ) 0.4 0.2 0 200 400 600 T , K Fig . 3. ( a ) Temperature variation of the thermal ...
... Thermal expansion coefficients ankl of CuGa3Ses versus cos2 at ( 1 ) 150 , ( 2 ) 300 , ( 3 ) 450 , and ( 4 ) 600 K. α × 106 , Κ - 1 15- 10 5 0 ( a ) -5- P ( b ) 0.4 0.2 0 200 400 600 T , K Fig . 3. ( a ) Temperature variation of the thermal ...
Trang 1453
... thermal expansion behavior of CuGa , Se , and Culn , Se , is similar to that of the ternary compounds CuGaSe2 and CuInSe2 [ 8 , 15-17 ] . The results we obtained are of interest to electronic engineers , since CuGa3Se , and CuIn , Se ...
... thermal expansion behavior of CuGa , Se , and Culn , Se , is similar to that of the ternary compounds CuGaSe2 and CuInSe2 [ 8 , 15-17 ] . The results we obtained are of interest to electronic engineers , since CuGa3Se , and CuIn , Se ...
Nội dung
Vol 47 No 10 2002 | 1456 |
Vol 47 No 11 2002 | 1603 |
Hydrothermal Synthesis of Nanocrystalline Powders | 1609 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
ų absorption acid analysis angles anion aqueous solution atoms band bond lengths calculated cations chelate Chem chemical cm-¹ complex composition compounds concentration coordination sphere corresponding crystal structure crystallographic curve decrease determined diffraction patterns dimers distances electron English Translation Copyright experimental formation formed g/cm³ H-bonds H₂O HCIO4 hydrogen bonds interaction ionic ions Khim ligands lithium MAIK Nauka/Interperiodica melting metal method mixture Mo atoms mol/l Moscow Nauk Neorg nitrate octahedra Original Russian Text oxide oxygen atoms perchlorate phase diagram phthalocyanine physicochemical pivalate pivalic acid plexes polyhedron proton Raman ratio reaction refined region Russia Received Russian Academy Russian Text Copyright salt samples sodium solid solutions solubility space group spectra spectrum studied synthesis Table temperature ternary thermal tion ture unit cell parameters values VD polyhedra vibrations water molecules X-ray diffraction X-ray powder diffraction