Russian Journal of Inorganic Chemistry, Tập 42,Số phát hành 1-4British Library Lending Division with the cooperation of the Royal Society of Chemistry, 1997 |
Từ bên trong sách
Kết quả 1-3 trong 35
Trang 18
... oxides show the mass transfer rate two orders of magnitude lower than oxides with M > 1.5 Å . Thus , regardless of the fact that crystal growth iso- therms for various oxides are seemingly similar , quan- titative analysis reveals ...
... oxides show the mass transfer rate two orders of magnitude lower than oxides with M > 1.5 Å . Thus , regardless of the fact that crystal growth iso- therms for various oxides are seemingly similar , quan- titative analysis reveals ...
Trang 182
... oxides in the gas phase , is nonadditive compared to the effects of individual oxides . The negative nonlinear deviation from additivity was interpreted in terms of the reciprocal effect of concurrent processes that is caused by a ...
... oxides in the gas phase , is nonadditive compared to the effects of individual oxides . The negative nonlinear deviation from additivity was interpreted in terms of the reciprocal effect of concurrent processes that is caused by a ...
Trang 307
... oxides reacted with nio- bium oxide at higher rates than the other rare - earth oxides . Their reactions with vanadium oxide were at a low rate , involving a prevailing diffusion of Pr and Tb ions . Oxide compounds based on rare - earth ...
... oxides reacted with nio- bium oxide at higher rates than the other rare - earth oxides . Their reactions with vanadium oxide were at a low rate , involving a prevailing diffusion of Pr and Tb ions . Oxide compounds based on rare - earth ...
Nội dung
Triple Molybdate Salts NaA3RM0O45 | 13 |
Synthesis and Properties | 21 |
Dynamics of Protoncontaining Groups in Tantalum Hydrogen Phosphate | 27 |
Bản quyền | |
18 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
absorption According acid addition analysis angles anion atoms bands barium nitrate bond calculated carbon cations changes Chem chemical Chemistry cm-¹ complexes composition compounds concentration considered constants containing coordination Copyright corresponding crystal curves decrease dependence determined diffraction distances effect electron energy equation exchange experimental fact formation fragments H₂O heating higher hydrogen increase indicates initial Inorganic interaction ions Journal Khim kinetic layer ligand measured melting metal method mixture mol/l Moscow Neorg Note observed obtained occur oxides oxygen atoms parameters peak phase Physics plexes polyhedra position powder precipitate pressure properties Publishing range ratio reaction REFERENCES region respectively Russian salts sample Sciences shift shows signals similar sodium solid solution space group spectra spectrum stability structure studied synthesis Table temperature tion transition Translation values vibrations X-ray