... indium ( I ) as a process for the chemical deposition of indium A N Red'kin , L G Dubovitskaya , V A Smirnov Institute for Problems in the Technology of Microelectronics and Highly Pure Materials , USSR Academy of Sciences ABSTRACT ...
... indium ( I ) as a process for the chemical deposition of indium A N Red'kin , L G Dubovitskaya , V A Smirnov Institute for Problems in the Technology of Microelectronics and Highly Pure Materials , USSR Academy of Sciences ABSTRACT ...
Trang 180
The thickness of the indium coating was calculated from the quantity of indium deposited on the support , assuming that it is uniformly distributed over the surface of known dimensions . The change in the electrochemical potential of ...
The thickness of the indium coating was calculated from the quantity of indium deposited on the support , assuming that it is uniformly distributed over the surface of known dimensions . The change in the electrochemical potential of ...
Trang 181
... indium on the support can thus be readily established ( see Table 1 ) . ( The conditions of the experiments were selected to minimise the liberation of indium in the bulk of the solution . ) The data in Table 1 show that under the ...
... indium on the support can thus be readily established ( see Table 1 ) . ( The conditions of the experiments were selected to minimise the liberation of indium in the bulk of the solution . ) The data in Table 1 show that under the ...
Nội dung
Journal | 1 |
The preparation of the anhydrous oxide chlorides ZrOCl2 and HfOCl2 | 10 |
Ts B Konunova L S Kachkar G F Serova | 16 |
Bản quyền | |
19 phần khác không được hiển thị
Ấn bản in khác - Xem tất cả
Thuật ngữ và cụm từ thông dụng
1989 Translated absorption acetylacetonates acid Akad aluminium anion aqueous solution atoms bands birefringence calculated cations Chem chemical Chemistry chloride cm-¹ cm¯¹ cm¹ coefficient complex formation components composition compounds concentration coordination sphere copper copper(II corresponding crystallisation crystals curves decrease determined diagram diffraction patterns DMSO electronic endothermic English translation enthalpy equilibrium ethylenediamine experimental formed given in Table groups H₂O hafnium heating hydrogen increase indium infrared spectra Inorg isothermal Khim lanthanide ligand magnetic magnetic susceptibility mass melts method mixture mol¹ molar molecules Moscow Nauk SSSR Neorg Neorganicheskoi Khimii 35 nickel(II niobium(V nitrate observed obtained oxide parameters phase transformation phosphinothricin Phys platinum(II precipitates proton range ratio reaction shows solid phases solid solutions solubility solvate specimens spectrum stability constants structure studied thermal analysis thermal decomposition TPPO Translated from Zhurnal translation in Russ values X-ray diffraction Zhurnal Neorganicheskoi Khimii ΣΣ